Products in Building Materials: Prepreg

NP193PM is composed of a 17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temperature phenolic resin matrix which includes a non-conducting solid lubricant. This composite has excellent mechanical strength at elevated temperatures and adverse environments. Applications include wear plates for conveyor systems, valve plates, and compressor and pump vanes.

High flexural, impact and tensile strengths, and very high flexural modulus. It is constructed of glass fabric impregnated with an epoxy resin system. NP512 is engineered to provide better physical properties than NEMA FR-4, and be more dimensionally stable than standard NP510A. Applications for this material are where enhanced flexural modulus and physical strength are desired.

17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temperature phenolic resin matrix, which produces a composite with excellent mechanical strength at elevated temperatures and adverse environments. Applications include wear plates for conveyor systems, valve plates, and compressor and pump vanes. Variations of this material may be developed for specific applications.

Basaltex NV Basaltex BAS1101 is an impregnated basalt fabric designed as fire barrier in composites for public transport, aerospace, maritime, automotive as well as building and construction. Basalt fibers are extruded from 100% basalt volcanic rocks. They are characterized by outstanding mechanical properties combined with unique heat resistance. Basalt fibers are inert at high temperatures, will not soften like glass fibers, and retain their structure as barrier in a fire.

Natex P-Preg PLA UD 800 is a powder-coated fabric woven from flax fibers that are pre-impregnated with thermoplastic resins. It comes as NATTEX® P-Preg, PolyLactic Acid with 1000 mm Width and pre-preg fabrics uni-directional in natural fibers with flax of 750 g/m2.

Unidirectional CARBON FIBER PRE-PREG TAPE may be stored at 72°F for 30 days and for maximum shelf life, store in a freezer and bring up to room temperature for fabrication.

HS Carbon Fiber UD250H60 is a E3 Matrix System with a precursor as PAN.

APCM DA 4518 E-Glass is a modified epoxy system coated on heavy weight unidirectional E-Glass fibers. This product is designed to build excellent unidirectional strength using a minimum number of plies. DA 4518/E-Glass Uni also features extended room temperature out time and service temperatures to 300°F.

AX-3112T is a High Toughness, Flame Retardant, Epoxy Fiberglass Prepreg.

AX-3270 is a Structural Epoxy Fiberglass Prepreg.

IM Carbon Fiber UD100 H60-MR60H is a E3 Matrix System with a precursor as PAN.

Ecotechnilin L-FLAXPREG-T-UD-110-5m² is a unidirectional (UD) fibers - FLAXPREG T-UD 110.

PREPREG system BD (epoxy resin) are based on modified epoxy resins with high impact strength and excellent dynamic properties. They can be processed into high-strength structural components using all common methods. The hardening range is between 85 ° C and 140 ° C ; the max. heat resistance is 125 ° C . The delivery program with fabric, laid and unidirectional reinforced PREPREGS allows the load-based design of your components.

IM Carbon Fiber UD200H60-MR70 is a E3 Matrix System with a precursor as PAN.

APCM DA 4517 is an epoxy prepreg designed for a temperature range of -67°F (-55°C) to 350°F (177°C), with a cure of 180°F (82°C) for three hour. Shorter cures times are available at higher temperatures. The system is designed to be post cured if the higher temperature service range is required.

IM Carbon Fiber UD150H60-MR60H is a E3 Matrix System with a precursor as PAN.

OM10 is highly toughened structural Low Tg resin for press and autoclave curing for the needs of structural parts used in Automotive Industry. OM10 prepreg cures at both press and Autoclave with long out-life of 4 weeks at ambient temperature.

IM Carbon Fiber UD125 H60-T800 GRADE is a E3 Matrix System with a precursor as PAN.

Natex P-Preg PP P1/1 900 is a powder-coated fabric woven from flax fibers that are pre-impregnated with thermoplastic resins. It comes as NATTEX® P-Preg, Polypropylene with 1000 mm Width and pre-preg fabrics uni-directional in natural fibers with flax of 900 g/m2.

APCM DA 4080 is 200°F cure modified epoxy prepreg system which can be prepreged on fiberglass fabric, woven Kevlar, or other woven fabrics. In addition to their low temperature cure capabilities, DA 4080 prepregs have excellent flow to allow for vacuum bag cure conditions. DA 4080 is a one sided pre-impregnated system yielding a single sided tack material. DA 4082 is the same system except that both sides of the fabric are coated yielding a double sided tack material. Both prepregs can be used for laminating and honeycomb sandwich construction.

EF 12 is above 240 °C. High Tg EF12 resin system is used to produce structural prepregs. Optimized cure methods for these resin systems are Press and Autoclave molding.

APCM DA 4090 is modified epoxy pre-impregnated system which can cure at 250°F (121°C) for one hour. DA 4090 | DA 4092 can be supplied on any commercially available glass, Kevlar, or graphite fabric. DA 4090 is a one sided pre-impregnated fabric yielding a single sided tack material. DA 4092 is the same system where both sides of the fabric are pre-impregnated yielding a double sided tack material. Both prepreg systems can be used for laminating and honeycomb sandwich construction.

IM Carbon Fiber UD200H60-T1000 GRADE is a E3 Matrix System with a precursor as PAN.

IM Carbon Fiber UD100H60-T800 GRADE is a E3 Matrix System with a precursor as PAN.

Plain weave CARBON FIBER PW 3K PRE-PREG may be stored at 75° F for a shelf life of 90 days and for maximum shelft life, sotre below 10° F for a maximum of 2 years and bring to room temperature for fabrication.

THINPREG™ TP 135 is a breakthrough product combining high strength and high toughness in a thin ply format. The PES-toughened epoxy system shows compression after impact properties typical of 3rd generation aerospace matrices. Thin ply materials achieve higher usable properties from the fiber through spreading load more consistently though the laminate and delaying first ply failure. Negligible ply drop-off effects and greater degrees of freedom in design are now combined with a PES-toughened system for high resolution, highly optimized, super-strong composite structures.

AX-3110 is a Toughened, Flame Retardant Epoxy Fiberglass Prepreg.

IM Carbon Fiber UD100H60-MR70 is a E3 Matrix System with a precursor as PAN.

HS Carbon Fiber UD300H60 is a E3 Matrix System with a precursor as PAN.

APCM DA 409U/G35-150 is a tough, versatile, modified epoxy resin prepreg that cures at 250°F, a standard modulus 150 g/m2 carbon prepreg tape which can also be supplied as a 200g/m2 or a 300 g/m2 prepreg.

Australian Composites Auspreg UV is a range of UV curable resin impregnated fiber glass prepregs which have been especially designed to cure from a wet plyable form to a completely hard product within minutes through exposure to either outdoors sunlight or high intensity artificial light. The technology is useful for repairing a whole range of surfaces and parts as a long term structural solution to wood, bitumen, concrete, metals and enables repair of damaged materials without the need for costly replacement. It is also highly effective in creating and manufacturing products in place of traditional hand lay up manufacturing, infusion systems, and oven cure methodologies.

THINPREG™ TP 513 is a prepreg resin matrix used for the manufacture of light weight prepreg molding materials. ThinPreg™ 513 is a versatile system that is used most often with carbon fiber, but can also be impregnated into a wide range of reinforcing fibers including quartz, glass, aramid etc.

Ecotechnilin L-FLAXPREG T-UD-50-5m² is a unidirectional (UD) fibers - FLAXPREG T-UD 50.

Ecotechnilin L-FLAXPREG-T-UD-110-36m² is a unidirectional (UD) fibers - FLAXPREG T-UD 70.

HS Carbon Fiber UD100H60 is a E3 Matrix System with a precursor as PAN.

OM14 is a fast curing structural prepreg for press curing for the needs of structural parts used in Automotive Industry. Its short curing cycle and hot de-moldable nature are especially optimized for mass production at Automotive Industry with the addition of exceptionally long out life at room temperature. OM14 eliminates the need of Autoclave and Cold storage plus it is especially optimized for mass production. New resin system not only cures under 1-2 minutes at 150°C at press under isothermal curing conditions but also hot de-moldable and long out-life of one year at ambient temperature.