Products in Other Infrastructure Applications: Prepreg

APCM DA 4092 is modified epoxy pre-impregnated system which can cure at 250°F (121°C) for one hour. DA 4090 | DA 4092 can be supplied on any commercially available glass, Kevlar, or graphite fabric. DA 4090 is a one sided pre-impregnated fabric yielding a single sided tack material. DA 4092 is the same system where both sides of the fabric are pre-impregnated yielding a double sided tack material. Both prepreg systems can be used for laminating and honeycomb sandwich construction.

APCM DA 409U/S2-glass is a tough, versatile, modified epoxy resin prepreg that cures at 250ºF. The S-2 glass is a Zentron High Strength fiber. Standard weight is 260g/m2 with a 38% resin content. Other weights and resin contents available upon request.

EF 12 is above 240 °C. High Tg EF12 resin system is used to produce structural prepregs. Optimized cure methods for these resin systems are Press and Autoclave molding.

OM 12 is a glass fiber or carbon fiber reinforced composites offer advantages of high corrosion resistance and high strength-to-weight ratio than traditional wood or steel materials. Kordsa may provide different reinforcement materials including glass or carbon UD, 2D and multiaxial impregnated with epoxy. For the huge size part production, generally vacuum bag only prepregs (OM12) are recommended

CM 15 is a Visual composites, Semi Structural and Fast Isothermally Press Curable, Class A Surface quality for painting, Hot Demoldable, Improved UV and environmental resistance, Improved fiber imprinting resistance

CM11 resin is Mid Tg and its prepregs are suitable for hot painting, hot gluing and cataphoresis processes. New resin system not only cures under 3 minutes at 150°C at press under isothermal curing conditions but also hot de-moldable and long out-life of two weeks at ambient temperature. These extreme conditions does not affect the visual Performance of prepreg system with CM11, capable of Class A Surface. Drapability is suitable for press molds and low to medium tack optimized for press curing.

OM14 is a fast curing structural prepreg for press curing for the needs of structural parts used in Automotive Industry. Its short curing cycle and hot de-moldable nature are especially optimized for mass production at Automotive Industry with the addition of exceptionally long out life at room temperature. OM14 eliminates the need of Autoclave and Cold storage plus it is especially optimized for mass production. New resin system not only cures under 1-2 minutes at 150°C at press under isothermal curing conditions but also hot de-moldable and long out-life of one year at ambient temperature.

EF 10 is highly toughened Mid Tg prepreg can be cured with autoclave and used in extreme applications in automotive industry and aviation industry.

APCM DA 4518U is a tough, versatile, modified epoxy resin system that cures at 250°F to 350°F. DA4518U can be supplied as a prepreg tape coated on unidirectional graphite.

APCM DA 4090 is modified epoxy pre-impregnated system which can cure at 250°F (121°C) for one hour. DA 4090 | DA 4092 can be supplied on any commercially available glass, Kevlar, or graphite fabric. DA 4090 is a one sided pre-impregnated fabric yielding a single sided tack material. DA 4092 is the same system where both sides of the fabric are pre-impregnated yielding a double sided tack material. Both prepreg systems can be used for laminating and honeycomb sandwich construction.

APCM DA 4517 is an epoxy prepreg designed for a temperature range of -67°F (-55°C) to 350°F (177°C), with a cure of 180°F (82°C) for three hour. Shorter cures times are available at higher temperatures. The system is designed to be post cured if the higher temperature service range is required.

OM10 is highly toughened structural Low Tg resin for press and autoclave curing for the needs of structural parts used in Automotive Industry. OM10 prepreg cures at both press and Autoclave with long out-life of 4 weeks at ambient temperature.

CM12 resin is Mid Tg, dicy-free fast cure, hot demoldable isothermal press curable resin system and it is suitable for sanding and metal composite hybrid part production. Drapability is suitable for press molds and low to medium tack optimized for press curing. Performance of prepreg system with CM12, capable of Class A Surface.

APCM DA 4080 is 200°F cure modified epoxy prepreg system which can be prepreged on fiberglass fabric, woven Kevlar, or other woven fabrics. In addition to their low temperature cure capabilities, DA 4080 prepregs have excellent flow to allow for vacuum bag cure conditions. DA 4080 is a one sided pre-impregnated system yielding a single sided tack material. DA 4082 is the same system except that both sides of the fabric are coated yielding a double sided tack material. Both prepregs can be used for laminating and honeycomb sandwich construction.

OM13 is a structural resin system. It is translucent when cured.

APCM DA 4518 is an epoxy prepreg designed for a temperature range of -67°F (-55°C) to 350°F (177°C), with a cure of 250°F (121°C) for one hour and or a cure of 350º F (177ºC) for 1 hour. This material needs to be post cure or cured to 350ºF to get the 350º properties.

OM11 is a resin structural Low Tg prepreg that specifically customized for fatigue resistance part production in Industry. OM11 prepreg materials can be curable with Autoclave and Press.

APCM DA 409U/G35-150 is a tough, versatile, modified epoxy resin prepreg that cures at 250°F, a standard modulus 150 g/m2 carbon prepreg tape which can also be supplied as a 200g/m2 or a 300 g/m2 prepreg.

OM 13SF is a Sandable surfacing film and autoclave curable, sandable, Class A giving surfacing film.

EF 11 is also optimized for press molding and used in extreme applications. The highest glass transition temperature reached with epoxy products.

APCM DA 4082 is 200°F cure modified epoxy prepreg system which can be prepreged on fiberglass fabric, woven Kevlar, or other woven fabrics. In addition to their low temperature cure capabilities, DA 4080 prepregs have excellent flow to allow for vacuum bag cure conditions. DA 4080 is a one sided pre-impregnated system yielding a single sided tack material. DA 4082 is the same system except that both sides of the fabric are coated yielding a double sided tack material. Both prepregs can be used for laminating and honeycomb sandwich construction.

APCM DA 4518 E-Glass is a modified epoxy system coated on heavy weight unidirectional E-Glass fibers. This product is designed to build excellent unidirectional strength using a minimum number of plies. DA 4518/E-Glass Uni also features extended room temperature out time and service temperatures to 300°F.