Identification & Functionality
- Chemical Family
- Chemical Name
- Plastics & Elastomers Functions
- CAS No.
- 12304-65-3
- EC No.
- 602-916-1
- Technologies
- Product Families
- Chemical Composition
Mg4.5Al2(OH)13(CO3)·3.5H2O (Basic Magnesium, Aluminum Carbonate Hydrate)
Features & Benefits
- Labeling Claims
- Materials Features
- Features
- Excellent feature of acid-absorption in polymers
- High transparency
- Good Dispersibility and no blooming
- Nontoxicity
Applications & Uses
- Markets
- Applications
- Compatible Polymers & Resins
- Application
Applicable Resin -PP, PE
Example of Using - Neutralizing Agent Heat-Retaining Agent
POPL No. - [B] NJ – 4737
- Application for Neutralization Agent
Features
Compared to calcium stearate which is used as neutralization agent too, HT-P is effective at low doses. HT-P doesn’t cause problems in using calcium stearate(bleeding of stearic acid, moisture absorption by CaCl2).
Evaluation of the degree of inactivation of residual acid materials
Less change of weight of iron test pieces (by oxidation) shows higher neutralization effect.Unit Blank
(non-stabilized PP)HT-P Calcium
StearateAddition amount ppm - 100 300 500 1000 Weight before test g 14.5195 14.6738 14.9310 14.4316 14.8497 Weight after test g 14.5329 14.6741 14.9311 14.4317 14.8499 Increment of weight g 0.0134 0.0003 0.0001 0.0001 0.0002 % 0.0922 0.0020 0.0007 0.0007 0.0013 
Properties
- Appearance
- White Powder
- Typical Properties
Value Units Test Method / Conditions Specific Surface Area (BET) 8 - 14 m2/g - Particle Size (150μｍ Pass) 100.0 % - Loss on Drying (105 °C, 2 hr.) max. 0.5 % - Refraction Index 1.50 -1.52 - - Beginning Temp. of Removing Crystallization Water Approx. 190 °C -
Technical Details & Test Data
- Heat-Retaining Property
Heat-Retaining Property
Hydrotalcites have infrared-absorbing ability. When they are added to agricultural PVC/ PE/ EVA films, heat-retaining property of these films is increased. Right-hand FT-IR spectra is PE films with 6.5 wt% HT-P and without HT-P.
Excellent Transparency
The reason is that the refractive indexes of hydrotalcites are almost as same as films itself, 1.5 .
Good Dispersibility
HT-series is treated the surface by higher fatty acid, and the median particle size is about 0.5 mm . Therefore, HT-series is mixed with films well.