Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 162 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 2.1 % ASTM D638 Tensile Modulus (at 5 mm/min) ¹¹ 14900 MPa ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 242 MPa ASTM D790 Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ 237 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 13700 MPa ASTM D790 Tensile Stress (Break, 5 mm/min) ¹¹ 172 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 2.2 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 15700 MPa ISO 527 Flexural Stress (Break, 2 mm/min) ¹¹ 264 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 13000 MPa ISO 178 Bonding Strength (TRI, 5 mm/min, Type A) ¹¹ 42 MPa ISO 19095 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.7 g/cm³ ASTM D792 Melt Volume Rate (at 275°C, 5 kg) ¹¹ 17 cm³/10 min ISO 1133 Melt Volume Rate (at 285°C, 5.0 kg) ¹¹ 27 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (Rate B/50) ¹¹ 216 °C ASTM D1525 Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ 208 °C ASTM D648 Vicat Softening Temperature (Rate A/50) ¹¹ 215 °C ISO 306 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 207 °C ISO 75/Af Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.000016 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.000017 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.000065 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.000068 1/°C ISO 11359-2 Relative Temperature Index (Electrical) ᵖ ¹¹ 75 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 75 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 75 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Dielectric Constant (at 1.1 GHz) ¹¹ 3.93 - SABIC method Dielectric Constant (at 1.9 GHz) ¹¹ 3.92 - SABIC method Dissipation Factor (at 1.1 GHz) ¹¹ 0.00792 - SABIC method Dissipation Factor (at 1.9 GHz) ¹¹ 0.00769 - SABIC method - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 980 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 123 J/m ASTM D256 Izod Impact (Notched, at -30°C) ¹¹ 115 J/m ASTM D256 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 60 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 12 kJ/m² ISO 180/1A Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ 10 kJ/m² ISO 180/1A Charpy Impact (Unnotched, at 23°C) ¹¹ 69 kJ/m² ISO 179/2C Charpy Impact (Notched, at 23°C) ¹¹ 12 kJ/m² ISO 179/2C Charpy Impact (Notched, at -30°C) ¹¹ 1.10E+01 kJ/m² ISO 179/2C - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 100 - 120 °C - Drying Time ⁷ 4 - 8 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 265 - 285 °C - Nozzle Temperature ⁷ 265 - 285 °C - Front - Zone 3 Temperature ⁷ 265 - 285 °C - Middle - Zone 2 Temperature ⁷ 260 - 280 °C - Rear - Zone 1 Temperature ⁷ 250 - 270 °C - Mold Temperature ⁷ 120 - 160 °C - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ min. 0.7 mm UL 94 - Note
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.