LNP STAT-KON™ Compound - DFD029 - SABIC's Specialty - PC

Enhanced TDS

Knowde-enriched technical product data sheet

Properties

Flame Rating

UL 94 V0

Physical Properties


	Value	Units	Test Method / Conditions
Density ¹¹	1.35	g/cm³	ISO 1183

Mechanical Properties


	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	75	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	4100	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	105	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	3700	MPa	ISO 178

Thermal Properties


	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000045	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000068	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	147	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	141	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Electrical Properties


	Value	Units	Test Method / Conditions
Surface Resistivity ᵈ ¹¹	10000 - 1000000000	Ω	ASTM D257

Impact Properties


	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80104, at 23°C) ¹¹	6	kJ/m²	ISO 180/1A

Injection Molding


	Value	Units	Test Method / Conditions
Back Pressure ⁷	0.2 - 0.3	MPa	-
Drying Temperature ⁷	120	°C	-
Drying Time ⁷	4	Hrs	-
Front - Zone 3 Temperature ⁷	320 - 330	°C	-
Maximum Moisture Content ⁷	0.02	%	-
Melt Temperature ⁷	305 - 325	°C	-
Middle - Zone 2 Temperature ⁷	310 - 320	°C	-
Mold Temperature ⁷	80 - 110	°C	-
Rear - Zone 1 Temperature ⁷	295 - 305	°C	-
Screw Speed ⁷	30 - 60	rpm	-

Flame Characteristics


	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	1.8	mm	UL 94

Note

ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.