Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break) ¹¹ 62 MPa ASTM D638 Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ 61 MPa ASTM D638 Tensile Strain (Break) ¹¹ 4.00E+00 % ASTM D638 Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 61 MPa ASTM D638 Tensile Modulus (at 50 mm/min) ¹¹ 3050 MPa ASTM D638 Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ 3.8 % ASTM D638 Flexural Stress ¹¹ 96 MPa ASTM D790 Flexural Stress ¹¹ 105 MPa ISO 178 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 4.1 % ASTM D638 Flexural Modulus ¹¹ 3170 MPa ASTM D790 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 107 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 3050 MPa ASTM D790 Tensile Stress (Yield, 5 mm/min) ¹¹ 63 MPa ISO 527 Tensile Strain (Yield, 5 mm/min) ¹¹ 4.3 % ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 8.6 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 3050 MPa ISO 527 Flexural Modulus (at 2 mm/min) ¹¹ 2890 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.32 g/cm³ ISO 1183 Density ¹¹ 1.31 g/cm³ ASTM D792 Specific Gravity ¹¹ 1.32 - ASTM D792 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.16 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.4 - 0.6 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.6 - 0.8 % ASTM D955 Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.24 % ISO 62 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 130 °C ASTM D648 Relative Temperature Index (Electrical) ᵖ ¹¹ 80 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 80 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 80 °C UL 746B Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 141 °C ASTM D648 Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ 0.000007 1/°C ASTM D696 Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ 0.000007 1/°C ASTM D696 Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 141 °C ISO 75/Bf Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 128 °C ISO 75/Af - Electrical Properties
Value Units Test Method / Conditions Surface Resistivity ᵈ ¹¹ 10 - 100000 Ω ASTM D257 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 2000 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 58 J/m ASTM D256 Multi-Axial Impact ¹¹ 5 J ISO 6603 Instrumented Dart Impact Total Energy (at 23°C) ¹¹ 12 J ASTM D3763 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 99 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 5 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 305 - 325 °C - Front - Zone 3 Temperature ⁷ 320 - 330 °C - Middle - Zone 2 Temperature ⁷ 310 - 320 °C - Rear - Zone 1 Temperature ⁷ 295 - 305 °C - Mold Temperature ⁷ 80 - 110 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94V-0 Flame Class Rating) ᵖ 1.6 mm UL 94 - Note
- ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability