ENYDYNE® H 88222 TA

ENYDYNE® H 88222 TA - Unsaturated polyester resin in styrene,DCPD. It is used to produce parts with high resistance to fire through hand lay up and spray up,injection molding,rtm method.

Brand: ENYDYNE (33 products)

Polymer Name: Polyester (unspecified)

Chemical Family: Polyesters, Unsaturated Polyester (UPE)

Processing Methods: Hand Lay-up, Resin Transfer Molding (RTM), Spray Lay-up

End Uses: Pipes, Tanks

Technical Data Sheet

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Chemical Family: Polyesters,
Unsaturated Polyester (UPE)
Polymer Name: Polyester (unspecified)
Composite Materials Functions: Resins, Binders & Matrix Materials
Technologies: Composite Materials
Product Families: Composite Materials — Polymers & Resins
Thermoset Resins

Features & Benefits

Product Highlights

Preaccelerated
Thixotropic

Properties

Typical Properties


	Value	Units	Test Method / Conditions
Solid Content	56 - 60	%	MT-CU001C
Specific weight at 20°C	1,11	g/cm3	-
Brookfield Viscosity at 23°C, sp 2 rpm 50	440 - 600	mPa.s	MT-CUT23V
Gel Time	20 - 25	minutes	MT-CU151R
Exothermic peak	135 - 155	°C	MT-CU151R
Reactivity at 23°C	+ 1,5	%	MEKP50
Peak (23°C)	28 - 33	-	-

Cured Properties


	Value	Units	Test Method / Conditions
Curing Cycle at 40°C + 2 h at 90°C (at 120°C for HDT))	16 (2)	hr	-
Tensile strength	-	MPa	ISO 527 (2012)
Tensile Modulus	3200	MPa	ISO 527 (2012)
Elongation at break	2	%	ISO 527 (2012)
Flexural strength	65	MPa	ISO 178 (2011)
Flexural modulus	2700	MPa	ISO 178 (2011)
HDT	55	°C	ISO 75 -2A (2013)

Safety & Health

Product Safety: Stir the resin before use, without use air bubbles

Storage & Handling

Shelf Life

6 Months (23°C in Dark )

Handling and Storage

Store in the shade, out of direct sunlight
Keep storage temperature below 25°C
Unseal container just before use
Shelf life will be reduced reaching higher temperature