Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Clear unaccelerated
Applications & Uses
- Markets
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
Value Units Test Method / Conditions Solid Content 64 - 68 % MT-CU001C Brookfield Viscosity at 25°C, sp 2 rpm 20 2450 - 2850 mPa.s MT-CUT25V Gel Time at 20°C + 1,5% MEKP50 160 - 200 minutes RS.08.G Exothermic peak at 20°C + 1,5% MEKP50 10-17 °C RS.08.G Acidity at 20°C + 1,5% MEKP50 10-17 mg KOH/g MT-CU001I Specific weight at 20°C 1,10 g/cm3 - - Cured Properties
Value Units Test Method / Conditions Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 60 MPa ISO 527 (2012) Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 3900 MPa ISO 527 (2012) Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 3800 MPa ISO 178/B (2010) Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 46 - ASTM D 2583 (2007) Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 120 MPa ISO 178/B (2010) HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 113 °C ISO 75 -2A (2013) Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 117 °C ASTM E 1545 (2011) Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 1,8 % ISO 527 (2012)
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature