Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Certificate RINA
- Preaccelerated
- Thixotropic
Applications & Uses
- Markets
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Color
- Typical Properties
Value Units Test Method / Conditions Specific weight at 20°C 01, 09 g/cm3 - Delta at 20°C + 1,5% MEKP50 7-11 minutes RS.08.G Exothermic peak at 20°C + 1,5% MEKP50 190 - 220 °C RS.08.G Brookfield Viscosity at 25°C, sp 2 rpm 20 450 - 700 mPa.s MT-CUT25V Solid Content 54 - 58 % MT-CU001C Gel Time at 20°C + 1,5% MEKP50 5-8 minutes RS.08.G - Cured Properties
Value Units Test Method / Conditions Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 3800 MPa ISO 527 (2012) Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 3800 MPa ISO 178/B (2010) HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 105 °C ISO 75 -2A (2013) Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 113 °C ASTM E 1545 (2011) Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 50 MPa ISO 527 (2012) Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 100 MPa ISO 178/B (2010) Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 46 - ASTM D 2583 (2007) Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C 1,6 % ISO 527 (2012)
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature