Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Features & Benefits
- UV light stable (minimal yellowing)
- Very low mixed viscosity of 980 cP
- Excellent electrical insulating characteristics
- Extremely high compressive and tensile strength
- Good adhesion to a wide variety of substrates, including metals, composites, glass, ceramics, and many plastics
- Solvent-free
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Mixing
- Measure 2 parts by volume of the part A and pour into the mixing container. Ensure all contents are transferred by scraping the container.
- Measure 1 part by volume of the part B and pour into the mixing container. Ensure all contents are transferred by scraping the container.
- Thoroughly and gently mix parts A and B together. Avoid introducing air bubbles.
- To de-air, let sit for 15 minutes or put in a vacuum chamber at 25 inHg for 2 minutes.
- If bubbles are present at the top, break them gently with the mixing paddle.
- Pour the mixture into a container holding the components to be protected.
- Close the part A and B containers tightly between uses to prevent skinning.
If crystallization/solidification occurs, reconstitute the product by warming to between 55 and 65 °C until it becomes fully re-liquified. Let the material cool to room temperature before mixing, to prevent flash cure.
Mixing >500 g at a time decreases working life and can lead to a flash cure. Limit the size of hand-mixed batches.
- Cure Instructions
Allow to dry at room temperature for 24 hours, or after letting sit for 10 minutes, cure the coating in an oven at one of these time/temperature options:
Temperature 65 °C 80 °C 100 °C Time 2 h 1 h 30 min
Properties
- Color
- Typical Properties
Value Units Test Method / Conditions Mix Ratio 2:1 Volume - Mix Ratio 2:1 Weight - Working Time 1 h - - Cured Properties
Value Units Test Method / Conditions Breakdown Voltage 41000 V - Compressive Strength 160 N/mm2 - CTE (After Tg) 192 ppm/˚C - CTE (Prior Tg) 80 ppm/˚C - Dielectric Constant (at 1 MHz) 3.2 - - Dielectric Strength 465 V/mil - Dissipation Factor (at 1 MHz) 0.03 - - Glass Transition Temperature (Tg) 33 °C - Hardness D 82 - - Intermittent Temperature -50 to 155 ˚C - Lap Shear (Aluminum) 6.8 N/mm2 - Lap Shear (Stainless Steel) 3.3 N/mm2 - Resistivity 1.6 x 10¹⁷ Ω·cm - Service Temperature Range (min. 65 may affect clarity) -40 to 140 ˚C - Tensile Strength 10 N/mm2 - Thermal Conductivity (at 25˚C) 0.2 W/(m·K) - - Uncured Properties
Value Units Test Method / Conditions Mixed Density 1.06 g/mL - Viscosity (at 25 ˚C) ⁽ᵃ⁾ 2.9 Pa·s - Viscosity (at 25 ˚C) ⁽ᵇ⁾ 0.3 Pa·s -
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Technical Details & Test Data
- Viscosity vs. Temperature
Packaging & Availability
Storage & Handling
- Shelf Life
- 5 Years
- Storage and Handling
- Store between 16 and 27 ˚C in a dry area, away from sunlight (see SDS).