Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Lubricating effect
- Dispersion
- Surface gloss
- Impact modification
Applications & Uses
- Markets
- Applications
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Use Level
- 0.25-0.5%
Properties
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Technical Details & Test Data
- Prime PA6
Formula
MFI (275℃, .16kg)
MFI
Change
Notched impact strength (23℃)
Impact strength change %
Tensile Strength
Breaking Elongation
Flexural Strength
Flexural Modulus
Testing Standard
GB/T 3682
GB/T 1843
GB/T
1040.4
GB/T
1040.4
GB/T 9341
GB/T 9341
Unit
g/10min
%
KJ/m2
%
MPa
%
MPa
MPa
PA6
54.40
0%
7.2
0%
76.6
28.1
79.4
2389
PA6+0.3% ST-PA9
97.92
80.0%
8.3
15.3%
76.2
37.3
82.4
2362
PA6+0.5% ST-PA9
111.60
105.0%
9.1
26.4%
76.8
44.4
86.6
2322
PA6+0.5% EBS
69.70
28.1%
6.9
-4.2%
77.9
26.3
82.6
2639
PA6+1% EBS
74.60
37.1%
7.0
-2.8%
83.5
27.2
84.1
2553
PA6+0.5% Silicone Powder
62.16
14.3%
7.0
-2.8%
78.4
24.6
86.7
2586
PA6+1% Silicone Powder
68.46
25.8%
7.1
-1.4%
84.6
25.8
87.8
2490
- PA6+30%GF
Formula
MFI (275℃, 2.16kg)
MFI
Change
Notched impact strength (23℃)
Impact strength change %
Tensile Strength
Elongation at Break
Flexural Strength
Flexural Modulus
Testing Standard
GB/T 3682
GB/T 1843
GB/T
1040.4
GB/T 1040.4
GB/T 9341
GB/T 9341
Unit
g/10min
%
kJ/m2
%
MPa
%
MPa
MPa
PA6+30%GF
25.5
0%
9.8
0%
143.0
7.0
204.0
6950
PA6+30%GF+0.3% ST-PA9
49.4
94.0%
11.0
12.2%
160.0
7.0
222.0
7850
PA6+30%GF+0.5% ST-PA9
69.6
173.0%
10.8
10.2%
163.0
7.2
226.0
8220
PA6+30%GF+0.5% EBS
28.0
9.8%
8.3
-15.3%
150.0
7.8
192.0
7292
PA6+30%GF+1% EBS
28.9
13.3%
8.9
-9.2%
153.2
7.9
195.8
7280
PA6+30%GF+0.5% Silicone
Powder
24.5
-3.9%
8.7
-11.2%
162.8
6.1
213.0
7617
PA6+30%GF+1% Silicone
Powder
27.2
-6.7%
9.3
-5.1%
163.3
6.7
218.3
7761
- PA66/PA6+30%GF
Formula
MFI (275℃, 2.16kg)
MFI
Change
Notched impact strength (23℃)
Impact strength change %
Tensile Strength
Elongation at Break
Flexural Strength
Flexural Modulus
Testing Standard
GB/T 3682
GB/T 1843
GB/T
1040.4
GB/T
1040.4
GB/T 9341
GB/T 9341
Unit
g/10min
%
kJ/m2
%
MPa
%
MPa
MPa
35%PA66+35%PA6+30%GF
31.1
0%
9.9
0%
163.0
7.1
202.0
6984
35%PA66+35%PA6+30%GF
+0.3% ST-PA9
60.2
93.5%
10.8
9.1%
178.0
7.0
226.0
7139
35%PA66+35%PA6+30%GF
+0.5% ST-PA9
65.7
111.3%
11.1
12.1%
167.0
7.2
221.0
7151
35%PA66+35%PA6+30%GF
+0.5%EBS
33.4
7.4%
11.2
13.1%
185.0
8.1
236.0
8216
35%PA66+35%PA6+30%GF
+1%EBS
35.8
15.1%
11.5
16.2%
189.2
8.3
240.1
8280
35%PA66+35%PA6+30%GF
+0.5% Silicone Powder
26.5
-14.8%
11.3
14.1%
162.4
7.5
221.0
7958
35%PA66+35%PA6+30%GF
+1% Silicone Powder
30.6
-1.6%
11.6
17.2%
167.3
7.7
224.1
7995