LAPOX

LAPOX® AC-14 is a chemically 2,4,6-tris(dimethyl aminomethyl) phenol. It is tertiary amine accelerator recommended to use along with other curing agents like polyamidoamides, amine adducts, mercaptans and anhydrides to increase cure speed. It improves cure of thin film and facilitate complete cure. The amount of Lapox AC-14 to be added into hardener depends on the speed of cure required.

LAPOX® AH-313 is a light-yellow aliphatic polyamine hardener suitable to cure epoxy resin at ambient temperature. When cured with epoxy resin it provides short pot life and faster cure speed. Due to very low viscosity and low dosage, it finds suitable for applications like adhesive, mortar and casting of small electrical components.

LAPOX® AH-315 is a long chain polyether amine having slow reactivity towards epoxy resin at ambient temperature. It is a clear colorless liquid with amine-like odor. It is miscible with water and soluble in many organic solvents. It provides long pot life and very low exotherm when cured with epoxy resins. Appropriately cured mass shows relatively high elongation, toughness, excellent resistance to impact and thermal shock resistance.

LAPOX® AH-341 is a modified aliphatic amine having low viscosity and light color. It is recommended for high solid and solvent free coatings. It has got excellent resistance to amine blushing under humid conditions. Due to low viscosity it is capable of high filler loading and good wetting properties. This hardener offers better area coverage, long working time with good glossy films.

LAPOX® AH-348 is a liquid, colorless aliphatic polyamine suitable to cure epoxy resins at room temperature. Epoxy resin cured with this hardener is capable to provide good resistance to aliphatic and aromatic hydrocarbon solvents and mild alkali solutions.

LAPOX® AH-351 is modified aliphatic amine adduct having high functionality, capable to cure epoxy resin at ambient temperature. It provides faster reactivity and short pot life when reacted with epoxy resins. When cured with stoichiometric ratio with modified epoxy phenol novolac, it provides high thermal and mechanical properties coupled with high chemical resistance. It is suitable to formulate solvent free and high solid coatings for high chemical resistance coatings and floorings.

LAPOX® AH-411 hardener is an ambient curing cycloaliphatic amine. Good color and color stability are the promising features of this curing agent, which produces films with non-blushing and excellent gloss.

LAPOX® AH-416 is a low color, low viscosity modified cycloaliphatic polyamine capable to cure epoxy resin at ambient temperature. The cured mass gives high gloss with an excellent surface finish suitable for protective and decorative coatings. The film withstand variety of chemicals includes acid, alkali, alcohols and hydrocarbon solvents. Excellent low color of the hardener makes suitable for self-leveling floor and decorative top coats.

LAPOX® AH-420 is a low color, low viscosity modified cycloaliphatic amine adduct. It suitable to cure epoxy resin at ambient temperature. It provides relatively faster reactivity and short pot life when cured with unmodified epoxy resins. It is mainly recommended for solvent-free and high solids coatings, gel coats and floor toppings. Good color and color stability are the promising features of this curing agent, which produces films with non-blushing and excellent gloss.

LAPOX® AH-424 is low color, low viscosity modified cycloaliphatic amine suitable to cure epoxy resin at ambient temperature. The faster reactivity of Lapox AH-424 permits rapid development of properties at ambient temperature. After cure, it exhibits high gloss with excellent surface finish suitable for coating and flooring application. The cured film has chemical resistance to acid, alkali, alcohols and hydrocarbon solvents. Very low viscosity permits high filler loading and excellent wetting properties. It is advisable to use this hardener during warm climate to avoid amine blush on cured surfaces.

LAPOX® AH-428 is a low color, low viscosity modified cycloaliphatic amine suitable to cure epoxy resin at ambient temperature. The cured mass gives high gloss with an excellent surface finish suitable for protective and decorative coatings. The film withstand variety of chemicals includes acid, alkali, alcohols and hydrocarbon solvents. Excellent low color of the hardener makes suitable for self-leveling floor and decorative top coats.

LAPOX® AH-440 is a modified cycloaliphatic amine available in form of low viscous transparent liquid. It is suitable to cure epoxy resins at ambient temperature. It is recommended for solvent free coating, floor topping, and industrial maintenance coatings along with modified or unmodified epoxy resins based on Bisphenol-A|F. Appropriately cured mass will provide excellent glossy films coupled with good mechanical strength and chemical resistance properties.

LAPOX® AH-543 (XH-80) is a light colored, low viscosity phenalkamine based on cashew nut shell liquid. It can able to cure modified and unmodified epoxy resin at room temperature as well as low temperatures up to 5°C. It is able to demonstrate good curing characteristic in presence of moisture and high humid conditions. When cured with epoxy resins it provides superior corrosion protection coupled with excellent film forming ability and adhesion to variety of substrates.

LAPOX® AH-711 is a high viscosity polyaminoamide hardener based on dimer fatty acid and aliphatic polyamine. It is designed to use with liquid or epoxy resin solutions (type-1) to produce protective and decorative solvent based coatings with an excellent flexibility and adhesion to most substrates.

LAPOX® AH-712 is medium viscosity polyamidoamide based on dimer fatty acid and aliphatic polyamine. It is designed to use with liquid or epoxy resin solutions (type-1) to produce protective and decorative solvent based coatings with an excellent flexibility, adhesion to most substrates and best corrosion protection.