E-Fibreglass Double Bias

E-Fiberglass Double Bias can be used in a variety of applications in the automotive, aerospace, construction, corrosive, industrial and marine industries. NCF is a composite reinforcing fabric in which fibers are organized into layers of plies of variable weight and orientation. The layers are stitched together. The result is a range of engineered fabrics with predictable, repeatable properties for the composite industry. The fiber orientation in the Double-Bias Non-Crimp Fabrics, ±450, is the optimum construction to provide high shear strength and stiffness. These materials are ideal for providing torsion stiffness in tubular constructions, or shear strength in the webs of beams or in stiffeners. As well as laterally loaded panels with aspect ratios from 1 to 3. Double-bias fabrics are also ideal products to use as tabbing material when bonding laminates together. This product is suitable for hand lay-up, vacuum bagging, vacuum injection, and other RTM- processes the fabric is very drapable and conforms well to complex geometry components.

Brand: E-Fibreglass (6 products)

Reinforcement Material: Glass Fibers

Reinforcement Form: Non Crimp Fabrics

Processing Methods: Hand Lay-up, Resin Transfer Molding (RTM), Vacuum Bagging

Features: Corrosion Resistance, Corrosion Resistant, High Stiffness, High Strength, High Torsional Stability

Technical Data Sheet

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Chemical Family: Glass Beads & Fibers
Reinforcement Form: Non Crimp Fabrics
Reinforcement Material: Glass Fibers
Composite Materials Functions: Reinforcement
Technologies: Composite Materials
Product Families: Composite Materials — Reinforcements
Glass Fiber

Features & Benefits

Materials Features: Corrosion Resistant,
High Stiffness,
High Strength,
High Torsional Stability

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Industrial
Applications: Automotive & Transportation — Automotive
Other Automotive Applications
Building & Construction — Building Materials
Other Building Materials,
Pipes & Plumbing,
Structural Components
Industrial — Chemical & Industrial Manufacturing
Other Industrial Applications
Automotive & Transportation — Transportation
Aerospace & Aviation,
Marine
Composites End Use: Beams
Composites Processing Methods: Hand Lay-up,
Resin Transfer Molding (RTM),
Vacuum Bagging

Properties

Physical Form: Fabric

Technical Details & Test Data

Fabric Specifications

XK0400 - 400gm Double-bias E-Glass
Layer Orientation degrees (°)	0	+45	90	-45
Layer Weight (gm/m2)	0	201	9	201
Material		E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)	8
Material	PES
Total weight (gm/m²)	419±3%
Standard roll width (mm)	1270

Fabric Specifications

XK0600 - 600gm Double-bias E-Glass
Layer Orientation degrees (°)	0	+45	90	-45
Layer Weight (gm/m2)	0	303	9	303
Material		E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)	11
Material	PES
Total weight (gm/m²)	625±3%
Standard roll width (mm)	1270

Fabric Specifications

XK0800 - 800gm Double-bias E-Glass
Layer Orientation degrees (°)	0	+45	90	-45
Layer Weight (gm/m2)	0	400	17	400
Material		E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)	8
Material	PES
Total weight (gm/m²)	825±5%
Standard roll width (mm)	1270

Typical Laminate Properties

TYPICAL LAMINATE PROPERTIES Laminate thickness 0.114 per 100gm/m²Fiber Fraction 50% by weight
	Test Method	₀o	+45^o	90^o	-45^o
Tensile Strength	ISO 3268	84* MPa	275 MPa	84* MPa	275 MPa
Tensile Modulus	ISO 3268	9,650* MPa	17,240 MPa	9,650* MPa	17,240 MPa
Compressive Strength	BS 2782	84* MPa	220 MPa	84* MPa	220 MPa
Compressive Modulus	BS 2782	9,650* MPa	17,240 MPa	9,650* MPa	17,240 MPa
Flexural Strength		84* MPa	372 MPa	84* MPa	372 MPa
Shear Strength, in plane	ASTM 4255-83	165 MPa	42 MPa	165 MPa	42 MPa
Shear Strength, interlamina	BS 2782	15.8 MPa	30.4 MPa
Elongation at break			2.9 %		2.9 %

Standard Stock

STANDARD STOCK
Order Code	Description	Roll Width	Roll Length
XK0400	400gm Double-bias E-Glass	1.27 m	75.2 Lm
XK0600	600gm Double-bias E-Glass	1.27 m	50.4 Lm
XK0800	800gm Double-bias E-Glass	1.27 m	38.6 Lm
X400T100	400gm Double-bias E-Glass tape	100 mm	75 Lm
X400T150	400gm Double-bias E-Glass tape	150 mm	75 Lm
X400T200	400gm Double-bias E-Glass tape	200 mm	75 Lm
X600T100	600gm Double-bias E-Glass tape	100 mm	50 Lm
X600T150	600gm Double-bias E-Glass tape	150 mm	50 Lm
X600T200	600gm Double-bias E-Glass tape	200 mm	50 Lm

Packaging & Availability

Packaging Type: Rolls

Storage & Handling

Storage

NCF Reinforcements should be stored on packaging roll, and kept dry and clean.