E-Fibreglass Biaxial

E-Fiberglass Biaxial can be used in a variety of applications in the automotive, aerospace, construction, corrosive, industrial and marine industries. NCF is a composite reinforcing fabric in which fibers are organized into layers of plies of variable weight and orientation. The layers are stitched together. The result is a range of engineered fabrics with predictable, repeatable properties for the composite industry. Longitudinal and Transverse (Biaxial) Non-Crimp Fabrics are Often used in the marine industry. They have similar fiber orientations to woven roving and combination woven roving / mat products, but do not have the fiber crimp associated with those woven products. This provides superior mechanical properties, particularly under fatigue loads. Biaxial (00/900) fabrics are available in much heavier weights than woven products. This speeds the cutting and laminating process, which saves significant fabrication costs. These materials are ideal in any application that requires optimum strength in two perpendicular directions. This product is suitable for hand lay-up, vacuum bagging of relatively flat components, vacuum injection, and other RTM-processes.

Brand: E-Fibreglass (6 products)

Reinforcement Material: Glass Fibers

Reinforcement Form: 0/90 Fabric, Non Crimp Fabrics

Processing Methods: Hand Lay-up, Resin Transfer Molding (RTM), Vacuum Bagging

Features: Corrosion Resistance, Corrosion Resistant, Fatigue Resistance, Fatigue Resistant, Good Mechanical Properties, Improved Mechanical Properties

Technical Data Sheet

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Chemical Family: Glass Beads & Fibers
Reinforcement Form: 0/90 Fabric,
Non Crimp Fabrics
Reinforcement Material: Glass Fibers
Composite Materials Functions: Reinforcement
Technologies: Composite Materials
Product Families: Composite Materials — Reinforcements
Glass Fiber

Features & Benefits

Materials Features: Corrosion Resistant,
Fatigue Resistant,
Good Mechanical Properties

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Industrial
Applications: Automotive & Transportation — Automotive
Other Automotive Applications
Building & Construction — Building Materials
Other Building Materials
Industrial — Chemical & Industrial Manufacturing
Other Industrial Applications
Automotive & Transportation — Transportation
Aerospace & Aviation,
Marine
Composites Processing Methods: Hand Lay-up,
Resin Transfer Molding (RTM),
Vacuum Bagging

Properties

Physical Form: Fabric

Technical Details & Test Data

Fabric Specifications

CK0400 - 400gm Biaxial E-Glass
Layer Orientation degrees (°)	0	+45	90	-45
Layer Weight (gm/m²)	236	0	174	0
Material	E-Glass		E-Glass

Weight, knitting yarn (gm/m²)	8
Material	PES
Total weight (gm/m²)	418±3%
Standard roll width (mm)	1270

Fabric Specifications

CK0600 - 600gm Biaxial E-Glass
Layer Orientation degrees (°)	0	+45	90	-45
Layer Weight (gm/m²)	295	0	307	0
Material	E-Glass		E-Glass

Weight, knitting yarn (gm/m²)	12
Material	PES
Total weight (gm/m²)	614±3%
Standard roll width (mm)	1270

Fabric Specifications

CK0800 - 800gm Biaxial E-Glass
Layer Orientation degrees (°)	0	+45	90	-45
Layer Weight (gm/m²)	404	0	397	0
Material	E-Glass		E-Glass

Weight, knitting yarn (gm/m²)	15
Material	PES
Total weight (gm/m²)	816±3%
Standard roll width (mm)	1270

Typical Laminate Properties

TYPICAL LAMINATE PROPERTIES Laminate thickness 0.114 per 100gm/m²Fiber Fraction 50% by weight
	Test Method	₀o	+45^o	90^o	-45^o
Tensile Strength	ISO 3268	275 MPa	85* MPa	275 MPa	85* MPa
Tensile Modulus	ISO 3268	17,240 MPa	9,650* MPa	17,240 MPa	9,650* MPa
Compressive Strength	BS 2782	220 MPa	85* MPa	220 MPa	85* MPa
Compressive Modulus	BS 2782	14,400 MPa		14,100 MPa
Flexural Strength		372 MPa		372 MPa
Shear Strength, in plane	ASTM 4255-83	42* MPa	165 MPa	66* MPa	165 MPa
Shear Strength, interlamina	BS 2782	34.4 MPa		29,600 MPa
Elongation at break		2.3 %		1.8%

Standard Stock

STANDARD STOCK
Order Code	Description	Roll Width	Roll Length
CK0400	400gm biaxial E-Glass	1.27 m	75.3 Lm
CK0600	600gm biaxial E-Glass	1.27 m	51.3 Lm
CK0800	800gm biaxial E-Glass	1.27 m	38.9 Lm

Packaging & Availability

Packaging Type: Rolls

Storage & Handling

Storage

NCF Reinforcements should be stored on packaging roll, and kept dry and clean.