INNOPOL® CS 1-3000 DEL

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Polymer Name

Polypropylene Homopolymer (HPP)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Homopolymer

Applications & Uses

Markets

Agriculture & Feed,

Building & Construction

Applications

Agriculture & Feed — Agricultural Films

Pipes & Hoses

Building & Construction — Building Materials

Pipes & Plumbing

Plastics & Elastomers End Uses

Pipes

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Black

Flame Rating

UL 94 HB

Physical Form

Solid

Flame Rating

UL 94 HB

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	0.92	g/cm3	ASTM D1505
Melt Mass Flow Rate - MFR (230°C/2.16kg)	8	g/10 min	ISO 1133
Molding Shrinkage - Parallel	1.1	%	ISO 1183
Molding Shrinkage - Across Flow	0.9	%	ISO 294-4
Melt Volume Flow Rate - MVR (230°C/2.16kg)	10	ml/10 min	ISO 1133

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (23°C)	4	kJ/m2	ISO 179/1eA
Tensile Stress at Yield (50 mm/min)	36	MPa	ISO 527-2
Charpy Impact Strength (23°C)	No Break	kJ/m2	ISO 179/1eU
Tensile Modulus (1 mm/min)	1600	MPa	ISO 527
Flexural Modulus (2 mm/min)	1800	MPa	ISO 178
Charpy Impact Strength (-30°C)	17	kJ/m2	ISO 179/1eU
Tensile Strain at Yield (50 mm/min)	8	%	ISO 527-1,-2
Nominal Tensile Strain at Break	15	%	ISO 527-1,-2
Charpy Notched Impact Strength (-30°C)	1.3	kJ/m2	ISO 179/1eA

Thermal Properties

	Value	Units	Test Method / Conditions
Melting Temperature (DSC)	162	°C	ISO 11357-3
Vicat Softening Temperature (A120)	152	°C	ISO 306
Vicat Softening Temperature (B120)	93	°C	ISO 306
Heat Deflection Temperature - HDT/A (1.8 MPa)	52	°C	ISO 75-1,-2
Heat Deflection Temperature - HDT/B (0.45 MPa)	101	°C	ISO 75-1,-2

Flammability

	Value	Units	Test Method / Conditions
Automotive Materials (thickness d ≥ 1 mm)	+	-	FMVSS 302
Burning Behaviour (d=3.2 mm)	HB	Class	UL-94

Other Properties

	Value	Units	Test Method / Conditions
Ash Content (600°C)	-	%	ISO 3451-1/A

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Injection Molding	-	-
Barrel Temperatures	190 to 230	°C	-
Injection Speed	Intermediate	-	-
Polymer Melt Temperature	210 to 240	°C	-
Mold Temperature	10 to 50	°C	-
Hold Pressure	50 – 100 % of actual injection pressure	-	-

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PPH	-	ISO 1043

Regulatory & Compliance

Certifications & Compliance

UL 94