Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Composites End Use
- Plastics & Elastomers End Uses
Properties
- Color
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Charpy Resistance With Notch (23°C) | 8.0 | Kj / m | ISO 179/2A |
Charpy Resistance Without Notch (23°C) | min. 100 | Kj / m | ISO 179/2 |
Flexural Modulus Of Elasticity (23°C) | 2000.0 | MPA | ASTM D 790 / ISO 178 |
Tensile Elongation (Break, 23°C) | min. 40 | % | ASTM D 638 / ISO 527 |
Tensile Strength (Yield, 23°C) | 50.0 | MPA | ASTM D 638 / ISO 527 |
Zod Resistance With Notch (23°C) | 90.0 | J / m | ASTM D 256 / ISO 180 |
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.1 | g / cm³ | ASTM D 792 / ISO 1183 |
Linear Shrinkage At Molding | 2.0 | % | Internal |
Water Absorption (24 h / 23°C) | 1.3 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Continuous Operating Temperature | 70.0 | °C | Whole |
Fusion Point | 258.0 | °C | Whole |
HDT (Deformation Temperature Under Load) (1.82 N/mm) | 75.0 | °C | ASTM D 648 / ISO 306 |
Vicat (Softening Temperature, 49 N) | 210.0 | °C | ASTM D 1525 / ISO 306 |
Value | Units | Test Method / Conditions | |
Flammability Class (3.2 mm) | HB | - | UL 94 |
Value | Units | Test Method / Conditions | |
CTI (Resistance To Creeping Currents) | min. 500 | V. | IEC 112 |
Dielectric Strength (2 mm) | 20.0 | Kv / mm | ASTM D 149 |
Volume Resistivity | 10^15 | Ohm * cm2 | ASTM D 257 |
Packaging & Availability
- Availability
Available in all colors as per sample or in the reference tables such as RAL or Pantone, reinforced with glass fibers, glass spheres or mixed fillers, elastomerized.
- PA 66 from yarn, high colorability, Ti02 free.
- PA 66 from yarn, Ti02 free, impact modified.
- PA 66 from yarn, fast cycles, Ti02 <0.3%.
- PA 66 from yarn, whitish, containing Ti02.
- PA 66 from yarn, Ti02 free, 15% glass fiber reinforced.
- PA 66 from yarn, Ti02 free, 30% glass fiber reinforced.
- PA 66 black from yarn with high characteristics.
- PA 66 black from aluminum modified yarn 'impact.
- PA 66 black from yarn, reinforced with 30% glass fiber.
- PA 66 black from yarn, reinforced with 30% SV, excellent surface appearance.