Properties
- Physical Properties
Value Units Test Method / Conditions Post Shrinkage (Parallel, Dam) 0.35 % Sim.ISO 294-4 Post Shrinkage (Normal, Dam) 0.6 % Sim.ISO 294-4 Density (Dam) 1.19 g/cm3 ISO 1183 - Mechanical Properties
Value Units Test Method / Conditions Unnotched Izod Impact Strength (at 23°C, 50% RH, Dam) 65 kJ/m2 ISO 180 Unnotched Izod Impact Strength (at -30°C, Dam) 63 kJ/m2 ISO 180 Tensile Strength (at Break, 5 mm/min, Dam) 230 MPa ISO 527 Tensile Modulus (at 1 mm/min, Dam) 16800 MPa ISO 527 Tensile Elongation (at Break, 5 mm/min, Dam) 3.5 % ISO 527 Notched Izod Impact Strength (at 23°C, 50% RH, Dam) 10 kJ/m2 ISO 180 Notched Izod Impact Strength (at -30°C, Dam) 7 kJ/m2 ISO 180 Flexural Stress (at 3.5% Strain, 2 mm/min, Dam) 310 MPa ISO 178 Flexural Modulus (at 2 mm/min, Dam) 12600 MPa ISO 178 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (at 50 N, 120°C/h, Dam) 235 °C ISO 306 Heat Deflection Temperature (at 8 MPa, 120°C/h, Dam) 180 °C ISO 75 Heat Deflection Temperature (at 1.8 MPa, 120°C/h, Dam) 225 °C ISO 75 Heat Deflection Temperature (at 0.45 MPa, 120°C/h, Dam) 240 °C ISO 75 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity (Dam) 0.5 Ohm*m IEC 60093 Surface Resistivity (Dam) 50000 Ohm IEC 60093 - Processing Parameters
Value Units Test Method / Conditions Mould Temperature 80 °C - Melt Temperature 265 - 275 °C - Drying Time 6 - 8 hrs Desiccant Dryer Drying Temperature 80 - 100 °C Desiccant Dryer
Safety & Health
- Processing Note
Under the recommended processing condition small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.