| Tensile Strength (Flow Direction) | 4.8 | MPa | ISO 37 |
| Elongation at Break (Flow Direction) | 530 | % | ISO 37 |
| Tensile Modulus at 100 % Elongation (Flow Direction) | 2.2 | MPa | ISO 37 |
| Tensile Modulus at 200 % Elongation (Flow Direction) | 2.7 | MPa | ISO 37 |
| Tensile Modulus at 300 % Elongation (Flow Direction) | 3 | MPa | ISO 37 |
| Tear Strength (Flow Direction) | 26.1 | kN/m | ISO 34-2 |
| Compression Set (22hr/70°C, Cross Flow) | 50 | % | ISO 815 |
| Tensile Strength (Cross Flow Direction) | 6.5 | MPa | ISO 37 |
| Elongation at Break (Cross Flow Direction) | 692 | % | ISO 37 |
| Tensile Modulus at 100 % Elongation (Cross Flow Direction) | 1.9 | MPa | ISO 37 |
| Tensile Modulus at 200 % Elongation (Cross Flow Direction) | 2.2 | MPa | ISO 37 |
| Tensile Modulus at 300 % Elongation (Cross Flow Direction) | 2.7 | MPa | ISO 37 |
| Tear Strength (Cross Flow Direction) | 24.4 | kN/m | ISO 34-2 |