Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- CASE Ingredients Functions
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Features
- Broad hardness range: Shore 00 to D 90
- Adjustable flow properties
- Filled and unfilled systems
- Good temperature cycle behavior
- Clear, UV-resistant systems
- Low dielectric constant
- Self-extinguishing systems in accordance with UL 94 V-0
- Good adhesion not only on conventional thermoplastics, but also on high-performance plastics such as LCP, BMC, etc.
- Operating temperature range: -60 °C to +165 °C
- Pot life adjustable from 1 to 90 minutes
- Thermal conductivity up to 2.0 W/m·K
Applications & Uses
Properties
- Typical Properties
Value Units Test Method / Conditions Density of Hardener at 22 °C 1.20 –1.24 g/cm³ DIN EN ISO 2811-1:2016-08 Thermal Conductivity 0.2 W/m·K DIN EN ISO 22007-2:2015-12 Volume Resistivity 10^13 Ω·cm DIN EN 62631-3-1:2017-01 Mixing Ratio 100 : 20 Parts by Weight - Operating Temperature –60 up to +120 °C - Water Absorption 0.2 % 30 days, 22 °C Coefficient of Expansion (<–70 °C) 80 ppm/K TMA ISO 11359-2:1999-10 Coefficient of Expansion (>–70 °C) 220 ppm/K - Density of Resin at 22 °C 0.93 – 0.95 g/cm³ DIN EN ISO 2811-1:2016-08 Dielectric Constant ε (at 50 Hz, 23 °C) 5.1 - DIN EN IEC 62631-2-1:2018-12 Dielectric Strength 20 kV/mm DIN EN 60243-1:2014-01 E modulus 2 N/mm² DIN EN ISO 527-2:2012-06 Glass Transition Temperature –65 °C TMA ISO 11359-2:1999-10 Loss Factor tan δ (at 50 Hz, 23 °C) 0.02 - DIN EN IEC 62631-2-1:2018-12 Mixed Viscosity at 22 °C 1800 – 2200 mPa·s Rotational viscometer Reactivity at 22 °C 3 – 40 min - Hardness 20 – 30 Shore A DIN ISO 7619-1:2012-02 Hardness 20 - 30 Shore A DIN ISO 7619-1:2012-02 - Flammability
Value Units Test Method / Conditions Flammability HB - UL 94