- Features
- Broad hardness range: Shore 00 to D 90
- Adjustable flow properties
- Filled and unfilled systems
- Good temperature cycle behavior
- Clear, UV-resistant systems
- Low dielectric constant
- Self-extinguishing systems in accordance with UL 94 V-0
- Good adhesion not only on conventional thermoplastics, but also on high-performance plastics such as LCP, BMC, etc.
- Operating temperature range: -60 °C to +165 °C
- Pot life adjustable from 1 to 90 minutes
- Thermal conductivity up to 2.0 W/m·K
Applications & Uses
Properties
- Typical Properties
Value Units Test Method / Conditions Density of Hardener at 22 °C 1.20 –1.24 g/cm³ DIN EN ISO 2811-1:2016-08 Operating Temperature –40 up to +130 °C - Dielectric Strength 30 kV/mm DIN EN 60243-1:2014-01 Coefficient of Expansion (<0 °C) 85 ppm/K TMA ISO 11359-2:1999-10 Coefficient of Expansion (>50 °C) 206 ppm/K - Density of Resin at 22 °C 0.99 –1.02 g/cm³ DIN EN ISO 2811-1:2016-08 Dielectric Constant ε (at 50 Hz, 23 °C) 3.4 - DIN EN IEC 62631-2-1:2018-12 Glass Transition Temperature 36 °C TMA ISO 11359-2:1999-10 Loss Factor tan δ (at 50 Hz, 23 °C) 0.033 - DIN EN IEC 62631-2-1:2018-12 Mixed Viscosity at 22 °C 1100 –1300 mPa·s Rotational viscometer Mixing Ratio 100 : 50 Parts by Weight - Reactivity at 22 °C 10 – 30 min - Thermal Conductivity 0.2 W/m·K DIN EN ISO 22007-2:2015-12 Water Absorption 0.4 % 30 days, 22 °C Hardness 50 – 60 Shore A DIN ISO 7619-1:2012-02 Hardness 50 - 60 Shore A DIN ISO 7619-1:2012-02 - Flammability
Value Units Test Method / Conditions Flammability HB - UL 94