POWERSIL® 466 A/B is suitable for production of electrically conductive injection molded articles, especially cable accessories in the medium and high voltage range. The range of use spreads from push-on accessories to cold shrink applications. POWERSIL® 466 A/B combines a low Shore A durometer with high elongation, good setting properties (low tension set) and good mechanical properties which are a must for cold shrink applications.
Processing
Components A and B are delivered ready to use in drums of 20 and 200 liters capacity. They can be pumped by means of standard metering equipment from these drums and mixing in a static mixer straight into the heated mold. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least three days.
Properties
- Catalyst Properties
Value Units Test Method / Conditions Dynamic Viscosity (A+B, Shear rate 10 s⁻¹) 550000 mPa·s DIN EN ISO 3219 Kick-Off Temperature (A+B) 125 °C - Pot Life (A+B, at 23°C) 3 days - - Cured Properties
Value Units Test Method / Conditions Compression Set (at 22 hours, 175°C) 11 % DIN ISO 815-1 type B method A Density 1.08 g/cm³ DIN EN ISO 1183-1 A Elongation (at break) 650 % ISO 37 Type 1 Modulus (at 100 % elongation) 0.75 N/mm² ISO 37 Type 1 Modulus (at 300 % elongation) 2.6 N/mm² ISO 37 Type 1 Shore Hardness A 38 - DIN ISO 48-4 Tear Strength 28 N/mm ASTM D 624 B Tensile Strength 7 N/mm² ISO 37 Type 1 Tension Set 2.6 % ISO 2285 Volume Resistivity 30 Ohm-cm IEC 62631-3-1 - Uncured Properties
Value Units Test Method / Conditions Dynamic Viscosity (Component A, Shear rate 10 s⁻¹) 600000 mPa·s DIN EN ISO 3219 Dynamic Viscosity (Component B, Shear rate 10 s⁻¹) 500000 mPa·s DIN EN ISO 3219 Mix Ratio (A:B) 1:1 parts by weight - - Properties
- High elongation at break, low tension set
- Stable electrical properties
- Good mechanical properties
- Ready-to-use, two-component system
- Note
Cured Properties: Cure conditions: 5 min / 165°C in press; Postcuring 4 h / 200°C.
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Packaging & Availability
- Country Availability
- Packaging Type
- Regional Availability
- Packaging Information
This product is available in 20 kg pail and 200 kg drum kits.