Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Ready-to-Use Product Features
- Specific Features
- Fast curing
- Heat resistant
- Low compression set without post-cure
- Reduced volatile content
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Applications
- General Automotive Parts
- Spark-Plug Boots
- Application Details
ELASTOSIL® LR 3094/60 A/B is particularly suitable for the economical production of large series of articles for the automotive industry, e.g. spark plug boots, distributor caps and various kinds of boots. Parts made from ELASTOSIL® LR 3094/60 A/B can generally be used for technical applications without post-curing, but do not comply with regulations concerning use in the pharmaceutical and food industry.
Processing
The A and B components are delivered ready to use in 20 kg pail and 200 kg drum kits. With adequate metering equipment, they can be pumped directly from the original containers into the injection molding machine and mixed by a static mixer. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least three days.
Properties
- Physical Form
- Cured Properties
Value Units Test Method / Conditions Compression Set (at 22 hours, 175°C) 18 % DIN ISO 815-1 type B method A Density 1.14 g/cm³ DIN EN ISO 1183-1 A Elongation (at break) 400 % ISO 37 Type 1 Shore Hardness A 60 - DIN ISO 48-4 Tear Strength 28 N/mm ASTM D 624 B Tear Strength 10 N/mm DIN ISO 34-1 method A Tear Strength 24 N/mm DIN ISO 34-1 method B Tensile Strength 10 N/mm² ISO 37 Type 1 - Uncured Properties
Value Units Test Method / Conditions Dynamic Viscosity (Shear rate 1 s⁻¹) 1300000 mPa·s DIN EN ISO 3219 Dynamic Viscosity (Shear rate 10 s⁻¹) 490000 mPa·s DIN EN ISO 3219 - Properties
ELASTOSIL® LR 3094/60 A/B contains a black heat stabilizer and therefore provides very good heat resistance. Vulcanizates show very low compression set even without post-curing.
- Note
Cure conditions : 5 min / 165°C in press.
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Packaging & Availability
- Country Availability
- Packaging Type
- Regional Availability
- Packaging Information
This product is available in 20 kg pail and 200 kg drum kits.
Storage & Handling
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.