Value Units Test Method / Conditions Tensile Stress at Yield MD* 11 MPa ISO 527-3 Tensile Stress at Yield TD* 12 MPa ISO 527-3 Tensile Stress at Break MD* 22 MPa ISO 527-3 Tensile Stress at Break TD* 20 MPa ISO 527-3 Elongation at Break MD* 400 % ISO 527-3 Elongation at Break TD* 600 % ISO 527-3 1% Secant Modulus MD* 180 MPa ISO 527-3 1% Secant Modulus TD* 190 MPa ISO 527-3 Elmendorf Tear Resistance MD* 45 N/mm ISO 6383-2 Elmendorf Tear Resistance TD* 60 N/mm ISO 6383-2 Impact Resistance F50 (Dart Drop Test)* 180 g ISO 7765-1/A Dynamic Coefficient Of Friction (COF)* min. 0.5 - ISO 8295 Haze* 6 % ISO 14782 Gloss (45°)* 70 % ASTM D 2457 Recommended Film Thickness* 0.25 micron - - Resin Properties
Value Units Test Method / Conditions Melt Flow Rate (190°C, 2.16kg) 0.8 g/10min ISO 1133 Density 0.924 g/cm³ ISO 1183 Melting Point 111 °C Internal Method Brittleness Temperature max. 75 °C ASTM D 746 Vicat Softening Point (1kg) 95 °C ISO 306/A