Vectorply E-LT 1800-P

E-LT 1800-P is a E-Glass fiber type.

Reinforcement Material: Glass Fibers

Reinforcement Form: 0/90 Fabric

Compatible Polymers & Resins: Polyesters, Vinyl Esters

Features: Corrosion Resistance, Corrosion Resistant, Cost Effective, High Impact Resistance, Light Weight, Lightweight

Technical Data Sheet

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Chemical Family: Glass Beads & Fibers
Reinforcement Form: 0/90 Fabric
Reinforcement Material: Glass Fibers
Composite Materials Functions: Reinforcement
Architecture: 0/90
Technologies: Composite Materials
Product Families: Composite Materials — Reinforcements
Glass Fiber

Features & Benefits

Materials Features: Corrosion Resistant,
Cost Effective,
High Impact Resistance,
Light Weight

Properties

Physical Form: Fabric
Dry Thickness: 0.022 (0.56)
Total Weight: 17.92 (608)
Roll Width: 50 (1270)
Roll Weight: 199 (90)
Roll Length: 122 (112)

Technical Details & Test Data

Fiber Architecture Data

0 ° : 8.96 oz/sq.yd / 304 g/sq.m
45 ° : n/a
90 ° : 8.96 oz/sq.yd / 304 g/sq.m
-45 ° : n/a
Chopped Mat : n/a

Laminated Properties

Laminate Weight

	E-LT 1800-P Resin Infused	E-LT 1800-P Open Mold
Fiber Resin Total	0.61 kg/sq.m 0.26 kg/sq.m 0.87 kg/sq.m	0.61 kg/sq.m 0.50 kg/sq.m 1.10 kg/sq.m

Physical Properties

	E-LT 1800-P Resin Infused	E-LT 1800-P Open Mold
Density Fiber Content Thickness	1.90 g/cc 52% by Vol. 0.5 mm	1.69 g/cc 37% by Vol. 0.7 mm

Laminate Modulii

	E-LT 1800-P Resin Infused	E-LT 1800-P Open Mold
Ex Ey Gxy Ex,flex. Ey,flex.	26.96 GPa 26.96 GPa 4.53 GPa 25.61 GPa 25.61 GPa	19.46 GPa 19.46 GPa 3.24 GPa 18.49 GPa 18.49 GPa

Ultimate Stress

	E-LT 1800-P Resin Infused	E-LT 1800-P Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear Long. Flex. Trans. Flex.	510.3 MPa 510.3 MPa 510.3 MPa 510.3 MPa 90.6 MPa 609.1 MPa 609.1 MPa	368.4 MPa 368.4 MPa 368.4 MPa 368.4 MPa 64.8 MPa 439.7 MPa 439.7 MPa

In-Plane Stiffness, "EA"

	E-LT 1800-P Resin Infused	E-LT 1800-P Open Mold
(EA)x (EA)y (GA)xy	12,302 N/mm 12,302 N/mm 2,068 N/mm	12,719 N/mm 12,719 N/mm 2,116 N/mm

Ultimate In-Plane Load

	E-LT 1800-P Resin Infused	E-LT 1800-P Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear	233 N/mm 233 N/mm 233 N/mm 233 N/mm 41 N/mm	241 N/mm 241 N/mm 241 N/mm 241 N/mm 42 N/mm