Value Units Test Method / Conditions Tensile Modulus (Dry) 2600 Mpa ISO 527-1 527-2 Charpy Notched Impact Strength (Dry-as-Mold Condition) 4 kg/m² ISO 179-1 Tensile Modulus (Condition) 940 Mpa ISO 527-1 527-2 Tensile Strain at Break (Dry) 45 % ISO 527-1 527-2 Tensile Strain at Break (Condition) max. 200 - - Tensile strain at yield (Dry) 5 % ISO 527-1 527-2 Tensile Strain at Yield (Condition) 24 % ISO 527-1 527-2 Flexural Modulus (Dry-as-Mold Condition) 2600 Mpa ISO 178 Flexural Strength (Dry-as-Mold Condition) 99 Mpa ISO 178 Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) 41 kg/m² ISO 179-1 Charpy Notched Impact Strength (Conditioned) 41 kg/m² ISO 179-1 Rockwell Hardness (Dry-as-Mold Condition) 112 R Scale ISO 2039 Charpy Notched Impact Strength (Dry) 4 kg/m² ISO 179-1 Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) 900 Mpa ISO 178 Flexural Modulus (Conditioned) 900 Mpa ISO 178 Tensile Modulus (Dry-as-Mold Condition) 2600 Mpa ISO 527-1 527-2 Flexural Modulus (Dry) 2500 Mpa ISO 178 Tensile Strain at Break (Dry-as-Mold Condition) 45 % ISO 527-1 527-2 Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) 34 Mpa ISO 178 Flexural Strength (Conditioned) 34 Mpa ISO 178 Tensile Strain at Yield (Dry-as-Mold Condition) 5 % ISO 527-1 527-2 Flexural Strength (Dry) 99 Mpa ISO 178 Tensile Stress at Yield (Dry-as-Mold Condition) 78 Mpa ISO 527-1 527-2 Rockwell Hardness (Conditioned to Equilibirium at 23°C, 50%RH) 88 R Scale ISO 2039 Rockwell Hardness (R Scale, Condtioned) 88 kg/m² ISO 2039 Rockwell Hardness (R Scale, Dry) 112 kg/m² ISO 2039 Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) 940 Mpa ISO 527-1 527-2 Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) max.200 % ISO 527-1 527-2 Tensile Strain at Break (Conditioned) max.200 % ISO 527-1 527-2 Tensile Strain at Yield (Conditioned to Equilibirium at 23°C, 50%RH) 24 % ISO 527-1 527-2 Tensile Strain at Yield (Conditioned) 24 % ISO 527-1 527-2 Tensile Strain at Yield (Dry) 5 % ISO 527-1 527-2 Tensile Stress at Yield (Conditioned to Equilibirium at 23°C, 50%RH) 38 Mpa ISO 527-1 527-2 Tensile Stress at yield (Conditioned) 38 Mpa ISO 527-1 527-2 Tensile Stress at yield (Dry) 78 Mpa ISO 527-1 527-2 - Thermal Properties
Value Units Test Method / Conditions Coefficient of Linear Thermal Expansion (Dry-as-Mold Condition) 9.6 10⁻⁵/°C ISO 11359-2 Deflection Temperature (Under load 0.45MPa) 151 °C ISO 75-2 Deflection Temperature (Under load 1.8MPa) 60 °C ISO 75-1 Coefficient of Linear Thermal Expansion 9.6 10⁻⁵/°C ISO 11359-2 Coefficient of Linear Thermal Expansion (Conditioned to Equilibirium at 23°C, 50%RH) 9.6 10⁻⁵/°C ISO 11359-2 - Typical Properties
Value Units Test Method / Conditions Mold Shrinkage (Thicknes:3.2mm, traverse) 1.3 % - Mold Shrinkage (Thickness : 3.2mm, Flow) 1 % - Mold Shrinkage (Thickness : 3.2mm, Transverse) 1.3 % - Water Absorption (23°C in Water 24H) 1.8 % ISO 62 Water Absorption (23°C, 50% RH Equilibirium) 2.8 % ISO 62 Density 1.13 g/cm³ ISO 1183 Flammability (mmt V-2) 0.84 - UL-94 - Electrical Properties
Value Units Test Method / Conditions Comparative Tracking Index (Conditioned to Equilibirium at 23°C, 50%RH) min. 600 - IEC 60112 Dielectric Constant (106Hz, Conditioned) 3.7 - IEC 60250 Dielectric Constant (106Hz, Dry) 3.4 - IEC 60250 Comparative Tracking Index (Dry-as-Mold Condition) min. 600 - IEC 60112 Dielectric Constant (Conditioned to Equilibirium at 23°C, 50%RH) 3.7 10⁶ Hz IEC 60250 Dissipation Factor (106Hz, Conditioned) 0.08 - IEC 60250 Dissipation Factor (106Hz, Dry) 0.02 - IEC 60250 Dissipation Factor (Conditioned to Equilibirium at 23°C, 50%RH) 0.08 10⁶ Hz IEC 60250 Dielectric Constant (Dry-as-Mold Condition) 3.4 10⁶ Hz IEC 60250 Electric Strength (Thickness:1mm, conditioned to Equilibirium at 23°C 50%RH) 33 MV/m IEC 60243-1 Dissipation Factor (Dry-as-Mold Condition) 0.02 10⁶ Hz IEC 60250 Electric Strength (Thickness:1mm, Conditioned) 33 MV/m IEC 60243-1 Electric Strength (Thickness:1mm, Dry-as-Mold Condition) 37 MV/m IEC 60243-1 Electric Strength (Thickness:1mm, Dry) 37 MV/m IEC 60243-1 Volume Resistivity (Conditioned to Equilibirium at 23°C, 50%RH) 8 x 10¹¹ Ω-m IEC 60093 Volume Resistivity (Conditioned) 8 x 10¹¹ Ω-m IEC 60093 Volume Resistivity (Dry) 3 x 10¹³ Ω-m IEC 60093 Volume Resistivity (Dry-as-Mold Condition) 3 x 10¹³ Ω-m IEC 60093 Comparative tracking Index min. 600 - IEC 60112