Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Form
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress at Break at +23°C 70-80 MPa ISO 527-2 Tensile Modulus at +23°C 3500-4500 MPa ISO 527-2 Izod Impact Strength, Notched (+23°C) 6-7 kJm2 ISO 180/A Tensile Strain at Break (+23°C) 3-4 % ISO 527-2 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (50 N) 200 °C ISO 306 Heat Deflection Temperature (1,80 Mpa) 180 °C ISO 75 Melting Temperature (10 K/Min) 225 °C ISO 11357 - Typical Properties
Value Units Test Method / Conditions Density 1.35-1.38 g/cm3 ISO 1183 Moisture Content max. 0.1 % ISO 15512 Molding Shrinkage (Normal) 1.2 % ISO 294-4 Molding Shrinkage (Parallel) 0.6 % ISO 294-4 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity 10000000000000000 Ohm.cm IEC 60093 Surface Resistivity 1.00E+14 Ohm IEC 60093 - Flammability
Value Units Test Method / Conditions Flame Rating (0,75 mm) HB - UL 94 Flame Rating (1,6 mm) HB - UL 94 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Predrying Temperature 100-120 °C - Predrying Time 4-8 hours - Melting Temperature 250-270 °C - Nozzle Temperature 240-260 °C - Pre-3 Region Temperature 240-260 °C - Mid-2 Region Temperature 230-250 °C - Aft-1 Region Temperature 230-240 °C - Mold Temperature 80-100 °C - Hold Pressure 40-80 MPa -