Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
Value Units Test Method / Conditions Tensile Strength (X -direction) 28 MPa ISO 527 -2 Tensile Modulus (X -direction) 1400 MPa ISO 527 -2 Tensile Elongation at Break (X -direction) 30 % ISO 527 -2 Flexural Modulus (X -direction) 1250 MPa DIN EN ISO 178 Charpy Impact Strength (notched,X -direction) 3.3 kJ/m² ISO 179 -1 Charpy Impact Strength (unnotched,X -direction) 29 kJ/m² ISO 179 -1 Izod Impact Strength (notched,X -direction) 3.5 J/m ISO 180 Izod Impact Strength (unnotched,X -direction) 24 J/m ISO 180 Tensile Strength (Z-direction) 28 MPa ISO 527 -2 Tensile Modulus (Z-direction) 1400 MPa ISO 527 -2 Tensile Elongation at Break (Z-direction) 10 % ISO 527 -2 Flexural Modulus (Z-direction) 1500 MPa DIN EN ISO 178 Charpy Impact Strength (notched,Z-direction) 3.2 kJ/m² ISO 179 -1 Charpy Impact Strength (unnotched,Z-direction) 20 kJ/m² ISO 179 -1 Izod Impact Strength (notched) / kJ/m² (Z-direction) 3 J/m ISO 180 Izod Impact Strength (unnotched) / kJ/m² (Z-direction) 16 J/m ISO 180 - Thermal Properties
Value Units Test Method / Conditions HDT/A (1.8 M Pa) 62 °C ISO 75 -2 HDT/B (0.45 MPa) 102 °C ISO 75 -2 Vicat/A (10 N) 131 °C ISO 306 Vicat/B (50 N) 90 °C ISO 306 - Typical Properties
Value Units Test Method / Conditions Bulk Density 330 kg/m³ DIN EN ISO 60 Printed Part Density 890 kg/m³ ISO 61 Mean Particle Size 60-70 d50/μm Laser Di_x001e_raction Melting Temperature 140 °C ISO 11357 ( 10 K/min) Crystallization Temperature 100 °C ISO 11357 ( 10 K/min) Melt Volume Flow Rate 14 cm³/10min ISO 1133 (2 20 °C, 2.16 kg)
Regulatory & Compliance
- Certifications
- ISO 9001:2015
- AS 9100:2016
- Controlled Goods Program