Silikal

SILIKAL® R 61 resin is a reactive, slightly elasticized resin for slip-resistant floorings in wet areas. SILIKAL® R 61 resin is a solvent-free, medium-viscosity 2-component methacrylic resin of a slightly elasticized character. It is employed as a binder in the manufacture of self-leveling coatings sprinkled with quartz sand or for smoothable floorings with colored quartz, predominantly in the food industry (wet areas), in coat thickness of 2 - 3 mm or 4 - 6 mm. Hot water stress is limited to 60 °C. This limit may be briefly exceeded to 80 °C for cleaning purposes, but only if the floor is not completely warmed through.

SILIKAL® R 62 resin is a medium-viscosity methacrylic resin that is outstandingly suitable for self-leveling coatings of 1 – 4 mm, predominantly indoors or as a top coat for elastic floorings outdoors. Coatings with SILIKAL® R 62 resin can bridge cracks to a certain degree. Visually appealing surfaces and systems can be developed when used in conjunction with a variety of fillers, pigments or decorative materials.

SILIKAL® RH 65 resin s a solvent free, fast curing MMA resin of very low viscosity. It is used for indoor screeds of 5-20 mm on concrete to equalize an uneven concrete surface. Screeds must be overlaid with a Silikal® coating system according to System A – E. The fast curing time of 1 hour, flexibility and filler rich formulation of 1 : 8 makes the mortar economical and can be applied at temperatures between 0°C and 35°C (refer to table of hardener). Hot water loadings must be limited to 60 °C. Excess temperature up to 80 °C will be accepted for a short moment as long as the temperature of the complete layer does not adopt the higher degree.

SILIKAL® RU 727 resin is a low-viscosity, transparent, solvent-free 3-component methacrylic resin with enhanced substrate adhesion.

SILIKAL® RV 368 resin is a solvent-free, 2-component methacrylic resin of high impact resistance and low-temperature fl exibility whose highly-molecular structure makes it outstandingly suitable for self-leveling coatings subject to extreme stresses, predominantly outdoors or for cold stores. Coatings made from SILIKAL® RV 368 resin are durably elastic and able to crack bridging.

SILIKAL® R 71 resin (SILIKAL® R 71 re resin) is a reactive, solvent-free, low-viscosity and almost non-yellowing 2-component me thacrylic resin offering high hardness and good resistance to chemicals. The extremely low viscosity enhances the penetrative capacity of the resin in sand-sprinkled surfaces. Its high hardness guarantees outstanding resistance to chemicals.

SILIKAL® R 81 resin is a reactive, solvent-free, low-viscosity, virtually non-yellowing 2-component methacrylic resin offering good resistance to water interaction. It serves primarily as a slightly elasticized and colorless top coat on sprinkled coatings in wet areas. The low viscosity enhances the penetrative capacity of the resin in sand-coated surfaces. Hot water stress is limited to +60 °C. The temperature stress may be increased to +80 °C for short periods, e. g. to allow cleaning, provided that the coating is not thoroughly warmed through to the substrate.

SILIKAL® R 82 resin is a reactive, solvent-free, low-viscosity, virtually non-yellowing 2-component methacrylic resin offering good resistance to water interaction. It serves primarily as a slightly elasticized and colorless top coat on sprinkled coatings in wet areas. The low viscosity enhances the penetrative capacity of the resin in sand-coated surfaces. Hot water stress is limited to +60 °C. The temperature stress may be increased to +80 °C for short periods, e. g. to allow cleaning, provided that the coating is not thoroughly warmed through to the substrate.