Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Key Features
- Cure temperature from 65°C to 120°C
- Service temperature up to 130°C after post cure
- Low CTE and shrinkage
- Work life at 20°C: 21 days
- Storage life at -18°C: 12 months
- Very low VOC content – no added solvents during manufacture
- Out of Autoclave
Applications & Uses
- Markets
- Applications
- Composites Processing Methods
- Typical Applications
General purpose – Visual – Out of Autoclave
Properties
- Typical Properties
Value Units Test Method / Conditions Cure Temperature 65 - 120 °C - Cure Time 16 - 1 - hrs,mins Outlife 21 - months Tg Onset 135 - - Tg Peak 140 - - Service Temperature 130 °C -
Technical Details & Test Data
- Cure Cycles and Performances
- Recommended Cure Cycle 1:
1 st dwell at 50°C for 1h, at a ramp rate of 1°C/min under full vacuum
2 nd dwell at 60°C for 1h, at a ramp rate of 1°C/min under full vacuum
3 rd dwell at 70°C for 10h, at a ramp rate of 1°C/min under full vacuum
- Recommended Cure Cycle 2:
1 st dwell at 50°C for 1h, at a ramp rate of 1°C/min under full vacuum
2 nd dwell at 60°C for 1h, at a ramp rate of 1°C/min under full vacuum
3 rd dwell at 70°C for 1h, at a ramp rate of 1°C/min under full vacuum
4 th dwell at 120°C for 1h, at a ramp rate of 1°C/min under full vacuum
Cure Initial Min Cure Tg 65°C (minimum) 16 hours 65°C 80°C 8 hours 80°C 100°C 2 hours 100°C 120°C (maximum) 1 hour 120°C 135°C Post-cure 2 hours 135°C *thin laminates only, to avoid exotherm – contact our technical team for advice.
- Curing Schedule is meant to be a guide only and is subject to local conditions.
- To avoid exotherm particular care must be taken with thick laminates.
Ramp rates must not exceed 1.0°C per minute during initial cure.
Ramp rates must not exceed 0.3°C per minute during post cure (free standing
Safety & Health
- Health And Safety
This material contains epoxy resin which can cause allergic reactions with skin contact and must avoid repeated and prolonged skin contact.
The following precautions must be taken when using epoxy resin prepregs:
- Overalls must be worn.
- Impervious gloves must be worn.
- Curing schedule is meant to be as a guide only and is subject to local conditions.
- To avoid exotherm, particular care must be taken with thick laminates.
- Ramp rates must not exceed 1.0°C/min during initial cure and 0.3°C/min during post cure.
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage and Out Life
This material should be kept frozen at -18°C. It must be kept sealed in a polythene bag which must not be opened until fully thawed to room temperature. If the material is not fully used, then the material must be resealed in the polythene bag to prevent moisture absorption.