Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Key Features
- Standard
- High Strength
- Dimentional Stability
- Excellent Ceramic/Metal Replacement
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers Processing Methods
- Typical Applications
In the electronics industry for the production of connectors, wiring device, frequency divider and a variety of instrument components, such as shell
- in the aerospace industry for the production of high strength, high temperature resistant and insulation of the high performance requirements of thin-walled parts;in the chemical industry for the production of corrosion-resistant valves, insulation devices in military products, for the production of precision electrical connectors, high strength, high temperature resistant contactor shell, motor module, pump impeller, pump, chemical pump etc.
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Strength 150 mPa ISO 527 Elongation at Break 1.7 % ISO 527 Flexural Modulus 14 GPa ISO 178 Flexural Strength 240 mPa ISO178 Charpy Impact Strength (V-notched) 8 kJ/m² IS0 179 - Thermal Properties
Value Units Test Method / Conditions Melting temperature (10°C/min) 280 °C ISO 11357 Heat Deflection Tem p High Load (1.8MPa) 260 °C ISO 75 Flammability V-0 class UL-94 - Typical Properties
Value Units Test Method / Conditions Density 1660 kg/m³ ISO 1183 Mold shrinkage (Machine Direction) 0.3 % GB/T 15585 Mold shrinkage (Transverse Direction) 0.7 % GB/T 15585 Water Absorption (23°C-sat) 0.02 % ISO 62 - Electrical Properties
Value Units Test Method / Conditions Dielectric Strength 16 KV/mm IEC 60243 Dielectric Constant 4.2 - IEC 60250 Dissipation Factor 0.002 - IEC 60250 Volume Resistivity 2×10^15 Ω.cm IEC 60093 CTI 150 V IEC 60112 - Processing Parameters
Value Units Test Method / Conditions Drying at 3h 150 °C - Injection Pressure 30~100 mPa - Injection Molding Melt Temperature 290~330 °C ISO 294 Injection Molding Melt Temperature 120~160 °C ISO 294 Limit in-cylinder retention time at 300°C min. 60 - - Limit in-cylinder retention time at 300°C min. 50 - -