Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Key Characteristics
Low smoke, low toxicity, halogen free, flame retardant thermoplastic compound mainly used in data and communication cables. Can also be used in LV power cable insulation and small diameter cable sheathing.
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Appearance
- Pellets
- Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 170 % IEC 60811-501 Elongation at Break (After Thermal Aging: 7 days at 110ºC) -10 % Variation IEC 60811-401 Tensile Strength (After Thermal Aging: 7 days at 110ºC) 12 % Variation IEC 60811-401 Tensile Strength (at Break) 13 N/mm² IEC 60811-501 - Physical Properties
Value Units Test Method / Conditions Density 1.5 g/cm³ BS EN ISO 1183-3 Melt Flow Rate (at 150°C / 21.6 kg) 14 g/10 min Internal Method Tear Strength 5 N/mm BS 6469-99.1 - Electrical Properties
Value Units Test Method / Conditions Dielectric Strength (at 20°C) 19.4 k/Vmm IEC 60243 Insulation Constant Ki Resistance (at 20ºC) 95 MOhm/km EN 50395 Insulation Constant Ki Resistance (at 90ºC) 0.065 MOhm/km EN 50395 Permittivity (50Hz at 23°C) 4.65 - IEC 60250 Volume Resistivity (at 20°C) 1.96 x 10¹⁴ Ohm.cm EN 50395 - Fire & Smoke Properties
Value Units Test Method / Conditions Halogen Acid Gas Evaluation max. 0.5 % IEC 60754-1 Limiting Oxygen Index 34 % BS ISO 4589-2 Smoke Density (3m Cube Test) Pass - BS EN 61034-2 Temperature Index 270 °C BS ISO 4589-3 Temperature Index 518 °F BS ISO 4589-3 - Thermo-Mechanical Properties
Value Units Test Method / Conditions Cold Bend (at -30°C) Pass No Cracks IEC 60811-504 Cold Impact (at -30°C) Pass - IEC 60811-506 Elongation at Break: (at -30°C) 50 (Pass) % IEC 60811-505 Hot Pressure Deformation (at 80°C) 15% % IEC 60811-508 - Fluid Resistance
Fluid Resistance Time (hrs) Temperature °C % Variation in Tensile Strength % Variation Elongation at Break ASTM No 2 4 70 18 7 1M NaOH 336 50 45 20 1M HCl 336 50 17 14
Technical Details & Test Data
- Processing
Extruder - An extruder with an L/D ratio (length/diameter) of 15-24 and an extruder screw with a compression ratio 1.2:1 to 2.5:1 are recommended.
Extruder Temperature Conditions - It is important that the melt temperature is not allowed to rise above 170°C. As a guide the following temperature profile is recommended:Zone #1 Zone #2 Zone #3 Zone #4 Head Die Celsius 130°C 140°C 145°C 150°C 160°C 160°C Fahrenheit 266°F 284°F 293°F 302°F 320°F 320°F This profile will vary slightly depending on extruder type, head design and output
Screw Water Temperature: Not mandatory, if present we recommend 40°-60°C Recommended Screen Pack: Spacer ring or breaker plate only
Head & Tool Design: The head and tools should be so designed as to allow streamlined flow of material. To obtain the optimum in physical properties in the case of tubing tools, a maximum draw down ratio of 1.5:1 is recommended to avoid internal stresses.Color Masterbatches: EVA, preferable, and PE based color masterbatches including black, up to a maximum of 1%, have no detrimental effect on the properties. It is recommended that all masterbatches should be thoroughly dried before use for 8 hours at 60°C or 4 hours at 80°C in a de-humidifying drier.
Packaging & Availability
Storage & Handling
- Storage & Shelf Life
This material has unlimited shelf life. The following storage conditions are recommended:
- Packaging should remain sealed
- Avoid storage outside and in direct sunlight.