Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, 50 mm/min) ¹¹ 64 MPa ISO 527 Tensile Stress (Break, 50 mm/min) ¹¹ 52 MPa ISO 527 Tensile Strain (Yield, 50 mm/min) ¹¹ 4 % ISO 527 Tensile Strain (Break, 50 mm/min) ¹¹ 18 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 2500 MPa ISO 527 Flexural Stress (Yield, at 2 mm/min) ¹¹ 98 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 2400 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.09 g/cm³ ISO 1183 Water Absorption (at 23°C, saturated) ¹¹ 0.15 % ISO 62-1 Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.06 % ISO 62 Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ 9 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ 0.000082 1/°C ASTM E831 Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ 0.000082 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ 0.000094 1/°C ASTM E831 Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ 0.000094 1/°C ISO 11359-2 Ball Pressure Test (at 123°C to 127°C) ¹¹ Pass - IEC 60695-10-2 Vicat Softening Temperature (Rate B/50) ¹¹ 149 °C ISO 306 Vicat Softening Temperature (Rate B/120) ¹¹ 138 °C ISO 306 Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ 129 °C ISO 75/Be Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 114 °C ISO 75/Af Relative Temperature Index (Electrical) ᵖ ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 65 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Relative Permittivity (1 MHz) ¹¹ 2.6 - IEC 60250 Relative Permittivity (1 MHz) ¹¹ 2.6 - ASTM D150 Dissipation Factor (at at 1 MHz) ¹¹ 0.0017 - ASTM D150 Dissipation Factor (at at 1 MHz) ¹¹ 0.0017 - IEC 60250 Dielectric Strength (shorttime, at 1mm) ¹¹ 46 kV/mm IEC 60243-1 - Processing Information (Profile Extrusion)
Value Units Test Method / Conditions Adapter Temperature 240 - 260 °C - Barrel - Zone 1 Temperature 220 - 240 °C - Barrel - Zone 2 Temperature 230 - 250 °C - Barrel - Zone 3 Temperature 240 - 260 °C - Barrel - Zone 4 Temperature 240 - 260 °C - Calibrator Temperature 50 - 70 °C - Die Temperature 240 - 260 °C - Drying Temperature 80 - 90 °C - Drying Time 2 - 3 Hrs - Hopper Temperature 40 - 60 °C - Melt Temperature 240 - 260 °C - - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 24 kJ/m² ISO 180/1A Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ 9 kJ/m² ISO 180/1A Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ 26 kJ/m² ISO 179/1eA Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ 11 kJ/m² ISO 179/1eA - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94V-1 Flame Class Rating) ʳ 1.5 mm UL 94 Oxygen Index (LOI) ʳ 34 % ISO 4589 - Note
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.