Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ 35 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹¹ 34 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ 8 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ 125 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹¹ 1240 MPa ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 51 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 1370 MPa ASTM D790 Tensile Stress (Yield, 50 mm/min) ¹¹ 35 MPa ISO 527 Tensile Strain (Break, 50 mm/min) ¹¹ 75 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 1370 MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 0.99 - ASTM D792 Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ 0.6 - 0.7 % SABIC method Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ 0.6 - 0.8 % SABIC method Melt Flow Rate (at 260°C, 5.0 kgf) ¹¹ 14 g/10 min ASTM D1238 Melt Volume Rate (at 260°C, 5.0 kg) ¹¹ 12 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (Rate B/50) ¹¹ 86 °C ASTM D1525 Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 112 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 85 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.000162 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.0000972 1/°C ASTM E831 Vicat Softening Temperature (Rate A/50) ¹¹ 131 °C ISO 306 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, at 23°C) ¹¹ 534 J/m ASTM D256 Instrumented Dart Impact Total Energy (at 23°C) ¹¹ 37 J ASTM D3763 Instrumented Dart Impact Total Energy (at -30°C) ¹¹ 30 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 60 - 65 °C - Drying Time ⁷ 2 - 4 Hrs - Drying Time (Cumulative) ⁷ 8 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 260 - 290 °C - Nozzle Temperature ⁷ 260 - 290 °C - Front - Zone 3 Temperature ⁷ 250 - 290 °C - Middle - Zone 2 Temperature ⁷ 240 - 280 °C - Rear - Zone 1 Temperature ⁷ 225 - 275 °C - Mold Temperature ⁷ 30 - 50 °C - Back Pressure ⁷ 0.3 - 0.7 MPa - Screw Speed ⁷ 20 - 100 rpm - Shot to Cylinder Size ⁷ 30 - 70 % - Vent Depth ⁷ 0.038 - 0.051 mm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ min. 1.5 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Regulatory & Compliance
- Certifications & Compliance