Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ 65 MPa ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ 55 % ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹¹ 57 MPa ASTM D638 Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ 100 MPa ASTM D790 Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ 5 % ASTM D638 Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ 2550 MPa ASTM D790 Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ 2450 MPa ASTM D790 Tensile Modulus (at 50 mm/min) ¹¹ 2250 MPa ASTM D638 Flexural Stress (Break, 2.6 mm/min, 100 mm span) ¹¹ 100 MPa ASTM D790 Tensile Stress (Yield, 50 mm/min) ¹¹ 66 MPa ISO 527 Tensile Strain (Break, 50 mm/min) ¹¹ 51 % ISO 527 Flexural Stress (Break, 2 mm/min) ¹¹ 98 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 2370 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 1.1 - ASTM D792 Melt Flow Rate (at 280°C, 2.16 kgf) ¹¹ 24 g/10 min ASTM D1238 Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ 65 g/10 min ASTM D1238 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 1.4 - 1.7 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 1.2 - 1.5 % ASTM D955 Water Absorption (at 23°C, 24hrs) ¹¹ 1.99 % ISO 62-1 Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹ 0.39 % ISO 62-4 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ 195 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.00009 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.000085 1/°C ASTM E831 Coefficient of Thermal Expansion (at 60°C to 138°C, flow) ¹¹ 0.000167 1/°C ASTM E831 Coefficient of Thermal Expansion (at 60°C to 138°C, xflow) ¹¹ 0.000153 1/°C ASTM E831 Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ 181 °C ISO 75/Be - Electrical Properties
Value Units Test Method / Conditions Dielectric Strength (in oil, at 1.6mm) ¹¹ 22.4 kV/mm ASTM D149 Dissipation Factor (at at 1 MHz) ¹¹ 0.017 - ASTM D150 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, at 23°C) ¹¹ 211 J/m ASTM D256 Izod Impact (Notched, at -30°C) ¹¹ 100 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 48 J ASTM D3763 Instrumented Dart Impact Energy (Peak, at -30°C) ¹¹ 32 J ASTM D3763 Izod Impact (Notched, 63.5*12.7*3.2, at 23°C) ¹¹ 13 kJ/m² ISO 180/4A Izod Impact (Notched, 63.5*12.7*3.2, at -30°C) ¹¹ 8 kJ/m² ISO 180/4A Charpy Impact (Notched, at 23°C) ¹¹ 21 kJ/m² ISO 179/2C Charpy Impact (Notched, at -20°C) ¹¹ 10 kJ/m² ISO 179/2C - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 100 - 120 °C - Drying Temperature ⁷ 95 - 105 °C - Drying Time ⁷ 3 - 4 Hrs - Drying Time ⁷ 2 - 3 Hrs - Drying Time (Cumulative) ⁷ 8 Hrs - Maximum Moisture Content ⁷ 0.07 % - Melt Temperature ⁷ 280 - 310 °C - Melt Temperature ⁷ 270 - 295 °C - Minimum Moisture Content ⁷ 0.02 % - Nozzle Temperature ⁷ 270 - 300 °C - Nozzle Temperature ⁷ 270 - 295 °C - Front - Zone 3 Temperature ⁷ 280 - 300 °C - Front - Zone 3 Temperature ⁷ 265 - 295 °C - Middle - Zone 2 Temperature ⁷ 270 - 290 °C - Middle - Zone 2 Temperature ⁷ 260 - 295 °C - Rear - Zone 1 Temperature ⁷ 260 - 280 °C - Rear - Zone 1 Temperature ⁷ 255 - 295 °C - Hopper Temperature ⁷ 60 - 80 °C - Mold Temperature ⁷ 80 - 120 °C - Mold Temperature ⁷ 65 - 95 °C - Back Pressure ⁷ 0.3 - 1.4 MPa - Screw Speed ⁷ 20 - 100 rpm - Shot to Cylinder Size ⁷ 30 - 50 % - Vent Depth ⁷ 0.013 - 0.038 mm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ 1.2 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.