Features & Benefits
- Materials Features
- Features
- High heatresistance (Tg in range of 155 to 195°C)
- Excellent processability with standard and high flow versions
- Ductile practical impact at low temperatures
- Excellent metallization capability
- Opaque and transparent colors
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Automotive Lighting (bezels, reflectors, inner lenses)
Properties
- Color
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ 70 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹¹ 60 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ 7 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ min. 25 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹¹ 2450 MPa ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 110 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 2600 MPa ASTM D790 Tensile Stress (Yield, 50 mm/min) ¹¹ 70 MPa ISO 527 Tensile Stress (Break, 50 mm/min) ¹¹ 60 MPa ISO 527 Tensile Strain (Yield, 50 mm/min) ¹¹ 7 % ISO 527 Tensile Strain (Break, 50 mm/min) ¹¹ min. 55 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 2400 MPa ISO 527 Flexural Stress (Yield, at 2 mm/min) ¹¹ 105 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 2350 MPa ISO 178 Ball Indentation Hardness (H358/30) ¹¹ 145 MPa ISO 2039-1 Hardness (Rockwell R) ¹¹ 125 - ISO 2039-2 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 1.2 - ASTM D792 Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ 0.6 - 0.9 % SABIC method Melt Flow Rate (at 300°C, 2.16 kgf) ¹¹ 37 g/10 min ASTM D1238 Melt Flow Rate (at 330°C, 2.16 kgf) ¹¹ 90 g/10 min ASTM D1238 Density ¹¹ 1.2 g/cm³ ISO 1183 Water Absorption (at 23°C, saturated) ¹¹ 0.25 % ISO 62-1 Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.25 % ISO 62 Melt Volume Rate (at 300°C, 2.16 kg) ¹¹ 33 cm³/10 min ISO 1133 Melt Volume Rate (at 330°C, 2.16kg) ¹¹ 85 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (Rate B/50) ¹¹ 155 °C ISO 306 Vicat Softening Temperature (Rate B/50) ¹¹ 155 °C ASTM D1525 Vicat Softening Temperature (Rate B/120) ¹¹ 156 °C ASTM D1525 Vicat Softening Temperature (Rate B/120) ¹¹ 1.58E+02 °C ISO 306 Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 150 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 138 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.00006 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.00006 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.00006 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.00006 1/°C ISO 11359-2 Thermal Conductivity (at 25°C) ¹¹ 0.2 W/m-°C ASTM C177 Ball Pressure Test (at 123°C to 127°C) ¹¹ Pass - IEC 60695-10-2 Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 150 °C ISO 75/Bf Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 138 °C ISO 75/Af Metallized Haze (Pass at 1.5mm) ¹¹ 145 °C SABIC method - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ No break J/m ASTM D4812 Izod Impact (Unnotched, at -30°C) ¹¹ No break J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 80 J/m ASTM D256 Izod Impact (Notched, at -30°C) ¹¹ 75 J/m ASTM D256 Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹ No break kJ/m² ISO 180/1U Izod Impact (Unnotched, 80*10*3, at -30°C) ¹¹ No break kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ 9 kJ/m² ISO 180/1A Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ 9 kJ/m² ISO 180/1A Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ 10 kJ/m² ISO 179/1eA Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ 10 kJ/m² ISO 179/1eA Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ No break kJ/m² ISO 179/1eU Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ No break kJ/m² ISO 179/1eU - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 130 °C - Drying Time ⁷ 4 - 6 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 290 - 335 °C - Nozzle Temperature ⁷ 285 - 330 °C - Front - Zone 3 Temperature ⁷ 290 - 335 °C - Middle - Zone 2 Temperature ⁷ 280 - 325 °C - Rear - Zone 1 Temperature ⁷ 270 - 315 °C - Mold Temperature ⁷ 85 - 130 °C - Back Pressure ⁷ 0.3 - 0.7 MPa - Screw Speed ⁷ 40 - 90 rpm - Shot to Cylinder Size ⁷ 40 - 60 % - Vent Depth ⁷ 0.025 - 0.08 mm - - Note
- ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.