Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ 58 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹¹ 67 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ 6 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ 142 % ASTM D638 Tensile Modulus (at 5 mm/min) ¹¹ 2260 MPa ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 98 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 2240 MPa ASTM D790 Hardness (Rockwell R) ¹¹ 120 - ASTM D785 Tensile Stress (Yield, 50 mm/min) ¹¹ 60 MPa ISO 527 Tensile Stress (Break, 50 mm/min) ¹¹ 73 MPa ISO 527 Tensile Strain (Yield, 50 mm/min) ¹¹ 6 % ISO 527 Tensile Strain (Break, 50 mm/min) ¹¹ 141 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 2080 MPa ISO 527 Flexural Stress (Yield, at 2 mm/min) ¹¹ 89 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 2070 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 1.2 - ASTM D792 Density ¹¹ 1.2 g/cm³ ISO 1183 Density ¹¹ 1.2 g/cm³ ASTM D792 Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ 0.5 - 0.7 % SABIC method Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ 7 g/10 min ASTM D1238 Water Absorption (at 23°C, saturated) ¹¹ 0.3 % ISO 62-1 Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.15 % ISO 62 Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ 6 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (Rate B/50) ¹¹ 130 °C ISO 306 Vicat Softening Temperature (Rate B/50) ¹¹ 136 °C ASTM D1525 Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 125 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 115 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.00008 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.00008 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.00008 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.00008 1/°C ISO 11359-2 Ball Pressure Test (at 123°C to 127°C) ¹¹ Pass - IEC 60695-10-2 Vicat Softening Temperature (Rate B/120) ¹¹ 131 °C ISO 306 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 115 °C ISO 75/Af Relative Temperature Index (Electrical) ᵖ ¹¹ 105 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 105 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 105 °C UL 746B - Optical Properties
Value Units Test Method / Conditions Light Transmission (at 2.54 mm) ¹¹ 88 % ASTM D1003 Haze (at 2.54 mm) ¹¹ max. 1 % ASTM D1003 Refractive Index ¹¹ 1.582 - ASTM D542 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, at 23°C) ¹¹ 966 J/m ASTM D256 Izod Impact (Notched, at -30°C) ¹¹ 899 J/m ASTM D256 Multi-Axial Impact ¹¹ 134 J ISO 6603 Instrumented Dart Impact Total Energy (at 23°C) ¹¹ 78 J ASTM D3763 Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹ No break kJ/m² ISO 180/1U Izod Impact (Unnotched, 80*10*3, at -30°C) ¹¹ No break kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ 72 kJ/m² ISO 180/1A Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ 63 kJ/m² ISO 180/1A Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ 82 kJ/m² ISO 179/1eA Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ 69 kJ/m² ISO 179/1eA Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ No break kJ/m² ISO 179/1eU Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ No break kJ/m² ISO 179/1eU - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 105 - 110 °C - Drying Time ⁷ 3 - 4 Hrs - Drying Time (Cumulative) ⁷ 24 Hrs - Melt Temperature ⁷ 260 - 305 °C - Nozzle Temperature ⁷ 255 - 300 °C - Front - Zone 3 Temperature ⁷ 260 - 305 °C - Middle - Zone 2 Temperature ⁷ 250 - 295 °C - Rear - Zone 1 Temperature ⁷ 240 - 280 °C - Mold Temperature ⁷ 50 - 80 °C - Back Pressure ⁷ 0.3 - 0.7 MPa - Screw Speed ⁷ 35 - 75 rpm - Shot to Cylinder Size ⁷ 40 - 60 % - Vent Depth ⁷ 0.038 - 0.076 mm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ min. 0.75 mm UL 94 - Note
- ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.