Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, 50 mm/min) ¹ 58.0 MPa ISO 527 Tensile Stress (Break, 50 mm/min) ¹ 54.0 MPa ISO 527 Tensile Strain (Yield, 50 mm/min) ¹ 9.0 % ISO 527 Tensile Strain (Break, 50 mm/min) ¹ 46.0 % ISO 527 Tensile Modulus (at 1 mm/min) ¹ 2154.0 MPa ISO 527 Flexural Modulus (at 2 mm/min) ¹ 2227.0 MPa ISO 178 Flexural Strength (2 mm/min) ¹ 91.0 MPa ISO 178 Tensile Modulus (at 50 mm/min) ¹ 2173.0 MPa ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹ 45.0 % ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹ 11.0 % ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹ 54.0 MPa ASTM D638 Tensile Stress (Yield, Type I, 50 mm/min) ¹ 58.0 MPa ASTM D638 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ 2120.0 MPa ASTM D790 Flexural Strength (2.6 mm/min, 100 mm span) ¹ 89.0 MPa ASTM D790 Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹ 2240.0 MPa ASTM D790 Hardness (Rockwell R) ¹ 118.0 - ASTM D785 Taber Abrasion (CS-17, 1 kg) ¹ 19.0 mg/1000cy ASTM D1044 - Physical Properties
Value Units Test Method / Conditions Density ¹ 1.09 g/cm³ ISO 1183 Moisture Absorption (23°C/50% RH/24hrs) ¹ 0.2 % ISO 62-4 Moisture Absorption (23°C/50% RH/Equilibrium) ¹ 0.57 % ISO 62-4 Water Absorption (23°C/saturated) ¹ 2.02 % ISO 62-1 Water Absorption (23°C/24hrs) ¹ 0.73 % ISO 62-1 Water Absorption (23°C/24hrs) ¹ 0.73 % ASTM D570 Mold Shrink (flow, annealed 130C 1hr) ¹ 1.1 - 1.5 % ASTM D955 Mold Shrinkage (flow, 3.2 mm) ¹ 0.9 - 1.2 % SABIC method Mold Shrinkage (xflow, 3.2 mm) ¹ 0.8 - 1.1 % SABIC method Melt Volume Rate (at 280°C/2.16 kg) ¹ 5.4 cm³/10 min ISO 1133 Melt Volume Rate (at 280°C/5.0 kg) ¹ 12.0 cm³/10 min ISO 1133 Specific Gravity ¹ 1.08 - ASTM D792 Water Absorption (23°C/Saturated) ¹ 2.81 % ASTM D570 Melt Flow Rate (at 280°C/2.16 kgf) ¹ 3.4 g/10 min ASTM D1238 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ 113.0 °C ISO 75/Af Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ 154.0 °C ISO 75/Bf Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ 120.0 °C ASTM D648 Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ 155.0 °C ASTM D648 Vicat Softening Temperature (at Rate B/50) ¹ 166.0 °C ISO 306 Vicat Softening Temperature (at Rate B/50) ¹ 200.0 °C ASTM D1525 Vicat Softening Temperature (at Rate A/50) ¹ 232.0 °C ASTM D1525 Vicat Softening Temperature (at Rate A/50) ¹ 235.0 °C ISO 306 Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹ 9.3e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹ 9.3e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -20°C to 150°C, flow) ¹ 9.0e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -20°C to 150°C, xflow) ¹ 9.3e-05 1/°C ASTM E831 Relative Temperature Index (Elec) ¹ 50.0 °C UL 746B Relative Temperature Index (Mech with impact) ¹ 50.0 °C UL 746B Relative Temperature Index (Mech w/o impact) ¹ 50.0 °C UL 746B - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched 80*10*4 +23°C) ¹ 18.0 kJ/m² ISO 180/1A Izod Impact (Unnotched 80*10*4 +23°C) ¹ NB kJ/m² ISO 180/1U Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹ 19.0 kJ/m² ISO 179/1eA Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹ NB kJ/m² ISO 179/1eU Izod Impact (Notched, 23°C) ¹ 220.0 J/m ASTM D256 Izod Impact (Notched, -30°C) ¹ 117.0 J/m ASTM D256 Izod Impact (Notched, -40°C) ¹ 53.0 J/m ASTM D256 Izod Impact (Unnotched, 23°C) ¹ 3204.0 J/m ASTM D4812 Izod Impact (Unnotched, -30°C) ¹ 3204.0 J/m ASTM D4812 Izod Impact (Unnotched, -40°C) ¹ 3204.0 J/m ASTM D4812 Instrumented Dart Impact Energy (at peak, 23°C) ¹ 46.0 J ASTM D3763 Instrumented Dart Impact Energy (at peak, -30°C) ¹ 36.0 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ³ 90 - 105 °C - Drying Time ³ 3 - 4 Hrs - Drying Time (Cumulative) ³ 8.0 Hrs - Maximum Moisture Content ³ 0.07 % - Minimum Moisture Content ³ 0.02 % - Melt Temperature ³ 275 - 300 °C - Rear - Zone 1 Temperature ³ 260 - 300 °C - Middle - Zone 2 Temperature ³ 265 - 300 °C - Front - Zone 3 Temperature ³ 270 - 300 °C - Nozzle Temperature ³ 275 - 300 °C - Mold Temperature ³ 65 - 95 °C - Back Pressure ³ 0.3 - 1.4 MPa - Screw Speed ³ 20 - 100 rpm - Shot to Cylinder Size ³ 30 - 50 % - Vent Depth ³ 0.013 - 0.038 mm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized 94HB Flame Class Rating ² min. 1.5 mm UL 94 - Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
(3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.