Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Strain (Break) ¹ 1.9 % ASTM D638 Tensile Strain (Break) ¹ 1.9 % ISO 527 Tensile Modulus (at 5 mm/min) ¹ 18200.0 MPa ASTM D638 Flexural Stress ¹ 300.0 MPa ASTM D790 Flexural Modulus ¹ 18000.0 MPa ASTM D790 Tensile Stress (Break) ¹ 200.0 MPa ISO 527 Tensile Stress (Break) ¹ 220.0 MPa ASTM D638 Tensile Modulus (at 1 mm/min) ¹ 20300.0 MPa ISO 527 Flexural Stress (Break, 2 mm/min) ¹ 360.0 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹ 17700.0 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹ 1.63 g/cm³ ASTM D792 Density ¹ 1.63 g/cm³ ISO 1183 Moisture Absorption (23°C/50% RH/24 hrs) ¹ 0.2 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ² 0.05 - 0.1 % ASTM D955 Mold Shrinkage (flow, 24 hrs) ² 0.06 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ² 0.08 - 0.2 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ² 0.15 % ISO 294 Spiral Flow (1mm) ¹ 30.0 cm SABIC method Spiral Flow (3mm) ¹ 70.0 cm SABIC method Moisture Absorption (23°C / 50% RH) ¹ 0.3 % ISO 62 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ 260.0 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ 1.2e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ 1.2e-05 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ 2.2e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ 2.2e-05 1/°C ISO 11359-2 Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ 275.0 °C ISO 75/Af - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, 23°C) ¹ 800.0 J/m ASTM D4812 Izod Impact (Notched, 23°C) ¹ 300.0 J/m ASTM D256 Multiaxial Impact ¹ 19.0 J ISO 6603 Instrumented Dart Impact Total Energy (at 23°C) ¹ 15.0 J ASTM D3763 Izod Impact (Unnotched 80*10*4 +23°C) ¹ 70.0 kJ/m² ISO 180/1U Izod Impact (Notched 80*10*4 +23°C) ¹ 38.0 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁴ 120 - 150 °C - Drying Time ⁴ 4.0 Hrs - Maximum Moisture Content ⁴ 0.15 % - Melt Temperature ⁴ 315 - 330 °C - Front - Zone 3 Temperature ⁴ 330 - 345 °C - Middle - Zone 2 Temperature ⁴ 320 - 330 °C - Rear - Zone 1 Temperature ⁴ 315 - 325 °C - Mold Temperature ⁴ 140 - 165 °C - Back Pressure ⁴ 0.2 - 0.3 MPa - Screw Speed ⁴ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized 94HB Flame Class Rating ³ min. 0.8 mm UL 94 - Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(3) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
(4) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
Regulatory & Compliance
- Certifications & Compliance