LNP™ VERTON™ Compound RX06424

LNP™ VERTON™ Compound RX06424 incorporates Polyamide 66 (nylon 66) resin with a high content of 60% long glass fiber, enhancing its mechanical properties significantly. Designed for easy molding, this compound offers manufacturers efficiency and versatility in processing. It is heat stabilized and UV stabilized, ensuring prolonged durability and performance in challenging environmental conditions. The structural reinforcement of LNP™ VERTON™ Compound RX06424 makes it suitable for applications where strength and reliability are critical, such as automotive components, industrial machinery, and outdoor equipment. This compound strikes a balance between robust mechanical strength, dimensional stability, and resistance to weathering, making it an excellent choice for demanding engineering applications requiring high-performance materials.

Brand: LNP™ VERTON™ Compound (48 products)

Polymer Name: Polyamide 66 (PA 66)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber

Technical Data Sheet

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Chemical Family
Fillers Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families

Features & Benefits

Applications & Uses

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Strain (Break) ¹1.6%ISO 527
Tensile Strain (Break) ¹1.6%ASTM D638
Tensile Modulus (at 50 mm/min) ¹19650.0MPaASTM D638
Flexural Stress ¹433.0MPaISO 178
Flexural Stress ¹430.0MPaASTM D790
Flexural Modulus ¹18920.0MPaISO 178
Flexural Modulus ¹18020.0MPaASTM D790
Tensile Stress (Break) ¹261.0MPaISO 527
Tensile Stress (Break) ¹270.0MPaASTM D638
Tensile Modulus (at 1 mm/min) ¹23280.0MPaISO 527
Physical Properties
ValueUnitsTest Method / Conditions
Density ¹1.71g/cm³ISO 1183
Density ¹1.71g/cm³ASTM D792
Moisture Absorption (23°C/50% RH/24 hrs) ¹0.44%ASTM D570
Mold Shrinkage (flow, 24 hrs) ²0.2%ASTM D955
Mold Shrinkage (flow, 24 hrs) ²0.2%ISO 294
Mold Shrinkage (xflow, 24 hrs) ²0.4%ASTM D955
Mold Shrinkage (xflow, 24 hrs) ²0.4%ISO 294
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹247.0 °C ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹1.7e-051/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹1.76e-051/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹5.3e-051/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹5.36e-051/°CASTM E831
Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹252.0°CISO 75/Bf
Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹252.0°CISO 75/Af
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Notched, 23°C) ¹412.0J/mASTM D256
Instrumented Dart Impact Energy (at peak, 23°C) ¹18.0JASTM D3763
Multiaxial Impact ¹18.0JISO 6603
Izod Impact (Unnotched 80*10*4 +23°C) ¹102.0kJ/m²ISO 180/1U
Izod Impact (Notched 80*10*4 +23°C) ¹54.0kJ/m²ISO 180/1A
Izod Impact (Notched 80*10*4 -40°C) ¹43.0kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ³80.0°C-
Drying Time ³4.0Hrs-
Maximum Moisture Content ³0.15 - 0.25%-
Melt Temperature ³290 - 305°C-
Front - Zone 3 Temperature ³290 - 300°C-
Middle - Zone 2 Temperature ³290 - 300°C-
Rear - Zone 1 Temperature ³280 - 295°C-
Mold Temperature ³95 - 110°C-
Back Pressure ³0.2 - 0.3MPa-
Screw Speed ³30 - 60rpm-
Note

(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wallmolding and gas-assist molding.