Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus (at 1 mm/min) 13230.0 MPa ISO 527 Tensile Stress (Yield) 220.0 MPa ASTM D638 Tensile Stress (Yield) 228.0 MPa ISO 527 Tensile Stress (Break) 220.0 MPa ASTM D638 Tensile Stress (Break) 228.0 MPa ISO 527 Tensile Strain (Yield) 2.3 % ASTM D638 Tensile Strain (Yield) 2.4 % ISO 527 Tensile Strain (Break) 2.3 % ASTM D638 Tensile Strain (Break) 2.4 % ISO 527 Tensile Modulus (at 50 mm/min) 14470.0 MPa ASTM D638 Flexural Stress 337.0 MPa ASTM D790 Flexural Stress 351.0 MPa ISO 178 Flexural Modulus 13000.0 MPa ISO 178 Flexural Modulus 12200.0 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Density 1.57 g/cm³ ASTM D792 Density 1.57 g/cm³ ISO 1183 Moisture Absorption (23°C/50% RH/24 hrs) 0.5 % ASTM D570 Mold Shrinkage (flow, 24 hrs) 0.2 - 0.4 % ASTM D955 Mold Shrinkage (flow, 24 hrs) 0.33 % ISO 294 Mold Shrinkage (xflow, 24 hrs) 0.7 - 0.9 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) 0.77 % ISO 294 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) 255.0 °C ISO 75/Af Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) 259.0 °C ISO 75/Bf Coefficient of Thermal Expansion (at -40°C to 40°C, flow) 2.1e-05 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) 2.16e-05 1/°C ASTM E831 Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) 256.0 °C ASTM D648 Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) 252.0 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) 4.86e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) 4.9e-05 1/°C ISO 11359-2 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched 80*10*4 +23°C) 23.0 kJ/m² ISO 180/1A Izod Impact (Unnotched 80*10*4 +23°C) 93.0 kJ/m² ISO 180/1U Multiaxial Impact 7.0 J ISO 6603 Izod Impact (Notched, 23°C) 265.0 J/m ASTM D256 Izod Impact (Unnotched, 23°C) 1409.0 J/m ASTM D4812 Instrumented Dart Impact Energy (at peak, 23°C) 14.0 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature 80.0 °C - Drying Time 4.0 Hrs - Maximum Moisture Content 0.15 - 0.25 % - Melt Temperature 290 - 305 °C - Front - Zone 3 Temperature 290 - 300 °C - Middle - Zone 2 Temperature 290 - 300 °C - Rear - Zone 1 Temperature 280 - 295 °C - Mold Temperature 95 - 110 °C - Back Pressure 0.2 - 0.3 MPa - Screw Speed 30 - 60 rpm -