Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break) ¹ 228.0 MPa ASTM D638 Tensile Strain (Break) ¹ 2.2 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹ 17440.0 MPa ASTM D638 Flexural Stress ¹ 296.0 MPa ASTM D790 Flexural Modulus ¹ 15230.0 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Density ¹ 1.61 g/cm³ ASTM D792 Mold Shrinkage (flow, 24 hrs) ² 0.2 % ASTM D955 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ 205.0 °C ASTM D648 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, 23°C) ¹ 1602.0 J/m ASTM D4812 Izod Impact (Notched, 23°C) ¹ 357.0 J/m ASTM D256 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ³ 80.0 °C - Drying Time ³ 4.0 Hrs - Maximum Moisture Content ³ 0.15 - 0.25 % - Melt Temperature ³ 265 - 275 °C - Front - Zone 3 Temperature ³ 275 - 290 °C - Middle - Zone 2 Temperature ³ 265 - 275 °C - Rear - Zone 1 Temperature ³ 250 - 260 °C - Mold Temperature ³ 80 - 95 °C - Back Pressure ³ 0.3 - 0.7 MPa - Screw Speed ³ 30 - 60 rpm - - Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.