Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break) ¹ 110.0 MPa ISO 527 Tensile Strain (Break) ¹ 2.2 % ISO 527 Tensile Modulus (at 1 mm/min) ¹ 7500.0 MPa ISO 527 Flexural Modulus ¹ 6000.0 MPa ISO 178 Flexural Stress (Yield, 2 mm/min) ¹ 135.0 MPa ISO 178 Flexural Stress (Break, 2 mm/min) ¹ 130.0 MPa ISO 178 Tensile Modulus (at 5 mm/min) ¹ 7100.0 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹ 2.8 % ASTM D638 Tensile Stress (Break, Type I, 5 mm/min) ¹ 95.0 MPa ASTM D638 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ 6100.0 MPa ASTM D790 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹ 135.0 MPa ASTM D790 Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹ 130.0 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Density ¹ 1.12 g/cm³ ISO 1183 Density ¹ 1.12 g/cm³ ASTM D792 Moisture Absorption (23°C / 50% RH) ¹ 0.008 % ISO 62 Water Absorption (23°C/saturated) ¹ 0.07 % ISO 62-1 Mold Shrinkage (flow, 24 hrs) ¹ 0.21 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ¹ 0.28 % ISO 294 Water Absorption (23°C/24hrs) ¹ 0.03 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ³ 0.21 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ³ 0.28 % ASTM D955 Wear Factor Washer ³ 44.0 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Dynamic Coefficient of Friction ³ 0.36 - ASTM D3702 Modified: Manual Static COF ³ 0.39 - ASTM D3702 Modified: Manual - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (at Rate B/50) ¹ 140.0 °C ISO 306 Vicat Softening Temperature (at Rate B/50) ¹ 140.0 °C ASTM D1525 Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ 157.0 °C ISO 75/Af Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ 164.0 °C ISO 75/Bf Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ 2.5e-05 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ 3.9e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ 8.0e-05 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ 7.1e-05 1/°C ASTM E831 Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ 156.0 °C ASTM D648 Relative Temperature Index (Elec) ² 65.0 °C UL 746B Relative Temperature Index (Mech with impact) ² 65.0 °C UL 746B Relative Temperature Index (Mech w/o impact) ² 65.0 °C UL 746B - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched 80*10*4 +23°C) ¹ 24.0 kJ/m² ISO 180/1A Izod Impact (Unnotched 80*10*4 +23°C) ¹ 42.0 kJ/m² ISO 180/1U Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹ 24.0 kJ/m² ISO 179/1eA Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹ 35.0 kJ/m² ISO 179/1eU Izod Impact (Notched, 23°C) ¹ 195.0 J/m ASTM D256 Izod Impact (Unnotched, 23°C) ¹ 460.0 J/m ASTM D4812 Multiaxial Impact ¹ 14.0 J ISO 6603 Instrumented Dart Impact Energy (at peak, 23°C) ¹ 8.0 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁴ 80.0 °C - Drying Time ⁴ 4.0 Hrs - Melt Temperature ⁴ 220 - 250 °C - Front - Zone 3 Temperature ⁴ 250 - 260 °C - Middle - Zone 2 Temperature ⁴ 245 - 255 °C - Rear - Zone 1 Temperature ⁴ 230 - 245 °C - Mold Temperature ⁴ 40 - 65 °C - Back Pressure ⁴ 0.2 - 0.3 MPa - Screw Speed ⁴ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized 94HB Flame Class Rating ² min. 1.5 mm UL 94 - Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
² UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
³ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
⁴ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.