Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 140 MPa ASTM D638 Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ 2.3 % ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 2.4 % ASTM D638 Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ 203 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 8650 MPa ASTM D790 Tensile Stress (Break, 5 mm/min) ¹¹ 140 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 2.2 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 9600 MPa ISO 527 Flexural Modulus (at 2 mm/min) ¹¹ 8160 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.55 g/cm³ ASTM D792 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.4 - 0.6 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 1 - 3 % ASTM D955 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 255 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 241 °C ASTM D648 Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 253 °C ISO 75/Bf Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 235 °C ISO 75/Af Relative Temperature Index (Electrical) ᵖ ¹¹ 130 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 105 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 115 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Comparative Tracking Index (UL, PLC) ¹¹ 3 PLC Code UL 746A Hot Wire Ignition (PLC 0) ¹¹ min. 3 mm UL 746A Hot Wire Ignition (PLC 1) ¹¹ min. 1.7 mm UL 746A High Ampere Arc Ignition (PLC 0) ¹¹ min. 3 mm UL 746A High Ampere Arc Ignition (PLC 1) ¹¹ min. 1.7 mm UL 746A High Voltage Arc Track Rate (PLC) ¹¹ 1 PLC Code UL 746A Arc Resistance (Tungsten, PLC) ¹¹ 7 PLC Code ASTM D495 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 604 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 67 J/m ASTM D256 Multi-Axial Impact ¹¹ 2 J ISO 6603 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 36 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 7 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 80 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Melt Temperature ⁷ 275 - 290 °C - Front - Zone 3 Temperature ⁷ 295 - 305 °C - Middle - Zone 2 Temperature ⁷ 280 - 295 °C - Rear - Zone 1 Temperature ⁷ 265 - 275 °C - Mold Temperature ⁷ 80 - 95 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94V-0 Flame Class Rating) ᵖ min. 1.7 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.