Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, 5 mm/min) ¹¹ 235 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 1.8 % ISO 527 Flexural Stress (Break, 2 mm/min) ¹¹ 335 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 19000 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Mold Shrinkage (flow) ᵍ ¹¹ 0.1 - 0.2 % SABIC method Density ¹¹ 1.7 g/cm³ ISO 1183 - Thermal Properties
Value Units Test Method / Conditions Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ 0.00001 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ 0.00006 1/°C ISO 11359-2 Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ 220 °C ISO 75/Ae - Electrical Properties
Value Units Test Method / Conditions Surface Resistivity ¹¹ 1.00E+14 Ω ASTM D257 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 65 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 14 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 80 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Melt Temperature ⁷ 265 - 275 °C - Front - Zone 3 Temperature ⁷ 275 - 290 °C - Middle - Zone 2 Temperature ⁷ 265 - 275 °C - Rear - Zone 1 Temperature ⁷ 250 - 260 °C - Mold Temperature ⁷ 80 - 95 °C - Back Pressure ⁷ 0.3 - 0.7 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Compliant (94HB Flame Class Rating) 0.8 mm UL 94 by SABIC-IP - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.