- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 203 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 1.8 % ASTM D638 Tensile Modulus (at 5 mm/min) ¹¹ 16700 MPa ASTM D638 Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ 285 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 15200 MPa ASTM D790 Tensile Stress (Break, 5 mm/min) ¹¹ 205 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 1.8 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 16800 MPa ISO 527 Flexural Strength (at 2 mm/min) ¹¹ 290 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 15400 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.7 g/cm³ ASTM D792 Melt Flow Rate (at 315°C, 5.0 kgf) ¹¹ 30 g/10 min ASTM D1238 Melt Volume Rate (at 315°C, 5.0 kg) ¹¹ 18 cm³/10 min ISO 1133 Specific Gravity ¹¹ 1.7 - ASTM D792 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.01 % ISO 62-4 Water Absorption (at 23°C, 24hrs) ¹¹ 0.02 % ISO 62-1 Water Absorption (at 23°C, 24hrs) ¹¹ 0.01 % ASTM D570 Mold Shrinkage (flow) ᵍ ¹¹ 0.2 - 0.3 % SABIC method Mold Shrinkage (xflow) ᵍ ¹¹ 0.4 - 0.5 % SABIC method - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 268 °C ASTM D648 Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 275 °C ASTM D648 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 270 °C ISO 75/Af Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 276 °C ISO 75/Bf Coefficient of Thermal Expansion (at -40°C to 90°C, flow) ¹¹ 0.000012 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 90°C, flow) ¹¹ 0.000013 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 90°C, xflow) ¹¹ 0.000041 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 90°C, xflow) ¹¹ 0.000043 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.000013 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.00004 1/°C ISO 11359-2 Relative Temperature Index (Electrical) ᵖ ¹¹ 130 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 130 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 130 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Dielectric Constant (at 1.9 GHz) ¹¹ 4.3 - SABIC method Dissipation Factor (at 1.9 GHz) ¹¹ 0.005 - SABIC method Dielectric Constant (at 5 GHz) ¹¹ 4.3 - SABIC method Dissipation Factor (at 5 GHz) ¹¹ 0.0058 - SABIC method - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, at 23°C) ¹¹ 145 J/m ASTM D256 Izod Impact (Unnotched, at 23°C) ¹¹ 650 J/m ASTM D4812 Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 15 kJ/m² ISO 180/1A Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 55 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at -40°C) ¹¹ 13.5 kJ/m² ISO 180/1A Izod Impact (Unnotched, 80*10*4, at -40°C) ¹¹ 50 kJ/m² ISO 180/1U Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ 15 kJ/m² ISO 179/1eA Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ 55 kJ/m² ISO 179/1eU - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 - 140 °C - Drying Time ⁷ 3 - 4 Hrs - Hopper Temperature ⁷ 50 - 70 °C - Melt Temperature ⁷ 310 - 330 °C - Front - Zone 3 Temperature ⁷ 310 - 330 °C - Middle - Zone 2 Temperature ⁷ 300 - 320 °C - Rear - Zone 1 Temperature ⁷ 290 - 300 °C - Mold Temperature ⁷ 135 - 160 °C - Back Pressure ⁷ 0.3 - 0.7 MPa - Screw Speed ⁷ 50 - 100 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94V-0 Flame Class Rating) ᵖ min. 0.4 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability