Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, 5 mm/min) ¹¹ 90 MPa ISO 527 Tensile Stress (Break, 5 mm/min) ¹¹ 85 MPa ISO 527 Tensile Strain (Yield, 5 mm/min) ¹¹ 2.7 % ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 3.4 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 5300 MPa ISO 527 Flexural Stress (Break, 2 mm/min) ¹¹ 144 MPa ISO 178 Flexural Strain (Break, at 2 mm/min) ¹¹ 4.9 % ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 4700 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Mold Shrinkage (flow) ᵍ ¹¹ 0.1 - 0.3 % SABIC method Density ¹¹ 1.31 g/cm³ ISO 1183 Water Absorption (at 23°C, 24hrs) ¹¹ 0.12 % ISO 62-1 - Thermal Properties
Value Units Test Method / Conditions Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ 0.00004 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ 0.000073 1/°C ISO 11359-2 Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 141 °C ISO 75/Bf Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 137 °C ISO 75/Af - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 45 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 6 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 305 - 325 °C - Front - Zone 3 Temperature ⁷ 320 - 330 °C - Middle - Zone 2 Temperature ⁷ 310 - 320 °C - Rear - Zone 1 Temperature ⁷ 295 - 305 °C - Mold Temperature ⁷ 80 - 110 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.