Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break) ¹¹ 136 MPa ASTM D638 Tensile Stress (Break) ¹¹ 136 MPa ISO 527 Tensile Strain (Break) ¹¹ 2.3 % ASTM D638 Tensile Strain (Break) ¹¹ 2.2 % ISO 527 Tensile Modulus (at 50 mm/min) ¹¹ 11810 MPa ASTM D638 Flexural Stress ¹¹ 204 MPa ASTM D790 Flexural Stress ¹¹ 203 MPa ISO 178 Flexural Modulus ¹¹ 11260 MPa ASTM D790 Flexural Modulus ¹¹ 10970 MPa ISO 178 Tensile Modulus (at 1 mm/min) ¹¹ 11170 MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.93 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.2 % ASTM D955 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.16 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.4 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.35 % ISO 294 Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.12 % ISO 62 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 136 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.0000325 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.0000326 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.000035 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.0000351 1/°C ISO 11359-2 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 137 °C ISO 75/Af - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 450 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 80 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 13 J ASTM D3763 Multi-Axial Impact ¹¹ 2 J ISO 6603 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 53 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 11 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 305 - 325 °C - Front - Zone 3 Temperature ⁷ 320 - 330 °C - Middle - Zone 2 Temperature ⁷ 310 - 320 °C - Rear - Zone 1 Temperature ⁷ 295 - 305 °C - Mold Temperature ⁷ 80 - 110 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.