Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 132 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 2.7 % ASTM D638 Tensile Modulus (at 5 mm/min) ¹¹ 9500 MPa ASTM D638 Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ 190 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 8400 MPa ASTM D790 Tensile Stress (Break, 5 mm/min) ¹¹ 125 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 2.2 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 9000 MPa ISO 527 Flexural Strength (at 2 mm/min) ¹¹ 185 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 7800 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.42 g/cm³ ASTM D792 Density ¹¹ 1.42 g/cm³ ISO 1183 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.1 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.1 % ASTM D955 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.11 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.5 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.48 % ISO 294 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 136 °C ASTM D648 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 140 °C ISO 75/Af - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 865 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 133 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 8 J ASTM D3763 Multi-Axial Impact ¹¹ 4 J ISO 6603 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 60 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 13 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 305 - 325 °C - Front - Zone 3 Temperature ⁷ 320 - 330 °C - Middle - Zone 2 Temperature ⁷ 310 - 320 °C - Rear - Zone 1 Temperature ⁷ 295 - 305 °C - Mold Temperature ⁷ 80 - 110 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.