PC based LNP THERMOCOMP™ compounds may be qualified to use in consumer electronics, industrial applications for combination of dimensional stability, thin wall and non-Br/Cl Eco FR systems.
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 154 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 2.1 % ASTM D638 Tensile Modulus (at 5 mm/min) ¹¹ 15320 MPa ASTM D638 Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ 223 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 13820 MPa ASTM D790 Tensile Stress (Break, 5 mm/min) ¹¹ 153 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 1.9 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 15130 MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.635 g/cm³ ASTM D792 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.05 - 0.2 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.05 - 0.2 % ASTM D955 Melt Volume Rate (at 300°C, 2.16 kg) ¹¹ 17 cm³/10 min ASTM D1238 Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ 48.6 g/10 min ASTM D1238 Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ 29 cm³/10 min ASTM D1238 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 107 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.0000139 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.0000415 1/°C ASTM E831 Relative Temperature Index (Electrical) ᵖ ¹¹ 80 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 80 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 80 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity ¹¹ 2.15E+16 Ω.cm ASTM D257 Surface Resistivity ¹¹ 5.00E+16 Ω ASTM D257 Dielectric Constant (at 1.1 GHz) ¹¹ 4.07 - SABIC method Dielectric Constant (at 1.9 GHz) ¹¹ 4.1 - SABIC method Dielectric Constant (at 5 GHz) ¹¹ 4.09 - SABIC method Dissipation Factor (at 1.1 GHz) ¹¹ 0.00762 - SABIC method Dissipation Factor (at 1.9 GHz) ¹¹ 0.00811 - SABIC method Dissipation Factor (at 5 GHz) ¹¹ 0.00896 - SABIC method - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 520 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 127 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 21 J ASTM D3763 Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ 12 kJ/m² ISO 179/1eA Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ 38 kJ/m² ISO 179/1eU - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 110 °C - Drying Time ⁷ 3 - 6 Hrs - Drying Time (Cumulative) ⁷ 12 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 285 - 310 °C - Nozzle Temperature ⁷ 285 - 305 °C - Front - Zone 3 Temperature ⁷ 280 - 300 °C - Middle - Zone 2 Temperature ⁷ 270 - 290 °C - Rear - Zone 1 Temperature ⁷ 260 - 280 °C - Mold Temperature ⁷ 80 - 110 °C - Back Pressure ⁷ 0.1 - 0.3 MPa - Screw Speed ⁷ 50 - 90 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94V-0 Flame Class Rating) ᵖ min. 1 mm UL 94 UL Recognized (94V-1 Flame Class Rating) ᵖ min. 0.8 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.