Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 212 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 2.8 % ASTM D638 Tensile Modulus (at 5 mm/min) ¹¹ 15000 MPa ASTM D638 Flexural Stress ¹¹ 310 MPa ASTM D790 Flexural Modulus ¹¹ 13000 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 1.55 - ASTM D792 Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ 0.12 % SABIC method Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ 0.44 % SABIC method Water Absorption (at 23°C, saturated) ¹¹ 0.8 % ISO 62-1 Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.15 % ISO 62 Melt Volume Rate (at 300°C, 2.16 kg) ¹¹ 15 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 2.50E+02 °C ASTM D648 Relative Temperature Index (Electrical) ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical with impact) ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical without impact) ¹¹ 65 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Dielectric Constant (at 1.1 GHz) ¹¹ 4 - ASTM ES 7-83 Dissipation Factor (at 1.1 GHz) ¹¹ 0.01 - ASTM ES 7-83 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, at 23°C) ¹¹ 150 J/m ASTM D256 Instrumented Dart Impact Total Energy (at 23°C) ¹¹ 12 J ASTM D3763 Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ 16 kJ/m² ISO 179/1eA - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 80 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Melt Temperature ⁷ 280 - 305 °C - Front - Zone 3 Temperature ⁷ 295 - 305 °C - Middle - Zone 2 Temperature ⁷ 280 - 295 °C - Rear - Zone 1 Temperature ⁷ 265 - 275 °C - Mold Temperature ⁷ 95 - 110 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ min. 0.8 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.